Rectangular lateral notches are not common engineering components, thus little research attention has been directed towards the investigation of their stress field properties. Indeed, no in-depth investigations have been conducted to date…
This is the third part of a short series of paper, revisiting some classical concepts of Linear Elastic Fracture Mechanics. Based on the solution for the single edge notched strip, discussed in Part-II, the present study deals with the…
Many engineering structures are exposed to non-proportional fatigue loading. However, at the critical location of crack initiation, often only one of the load sequences dominates – the individual load cases result in different crack…
The effect of corrosion environment aggressiveness on the tensile mechanical properties degradation of AA2024-T3 was investigated. Tensile specimens were pre-corroded for various exposure times to different corrosive solutions, i.e.…
The paper deals with the three-dimensional nature and the multi-parametric representation of the stress field ahead of cracks and notches of different shape. Finite thickness plates are considered, under different loading conditions. Under…
The presence of notches and other stress concentrations in turbine blades and other notch hydraulic components is a current problem in engineering. It causes a reduction of endurance limit of material. In that sense, specimens of the ASTM…
Several methods can be used to estimate elastoplastic (EP) notchtip stresses and strains from linear elastic calculations, providing EP stress and strain concentration factors. For uniaxial load histories, Neuber’s and Glinka’s rules are…
Numerous components designed for use at elevated temperatures now exhibit multiaxial stress states as a result of geometric modification and material inhomogeneity. It is necessary to anticipate the creep rupture life of such components…
A large number of mechanical components are subjected to fatigue loading beyond 106 cycles. The VHCF behaviour of smooth specimens has been extensively investigated in the recent years, even if more efforts are necessary to reveal the…
This paper presents a numerical method for non-local stress assessment by means of a general FE tool and the local stress field. Unlike usual calculations by means of a numerical PDE solver, a more general numerical integration is used.…
A criterion for the prediction of the static failure loads in tensile PMMA specimens with sharp notches is presented. The proposed criterion is based on a regularized version of the eXtended Finite Element Method (XFEM), which has been…
This paper addresses the estimation of critical loads in FFF (Fused Filament Fabrication) printed polymers and composites containing notches. Particularly, the analysis is focused on the fracture load estimations of 39 PLA (polylactic…
Engineering components often contain notches, keyways or other stress concentration features. These features raise the stress state in the vicinity of their apex which can lead to unexpected failure of the component. The Theory of Critical…
High resolution synchrotron X-ray tomography has been used to obtain 3D images of arrested cracks initiated at small artificial defects located on the surface of cylindrical steel specimens subjected to mode I fatigue loading. These…
Contacts with sharp edges subject to oscillatory loading are likely to nucleate cracks from the corners, if the loading is sufficiently severe. To a first approximation, the corners behave like notches, where the local elastic behaviour is…
Fatigue crack growth (FCG) is linked to irreversible and non-linear processes happening at the crack tip, which explains different problems observed in the use of da/dN-DK curves. The replacement of DK by non-linear crack tip parameters…
Notches and cracks are usually approximately modeled as two-dimensional problems using solutions from plane elasticity to quantify localized stress/strain concentration effects around their tips. However, they may be associated with high…
As often done in design practice, the Wöhler curve of a specimen, in the absence of more direct information, can be crudely retrieved by interpolating with a power-law curve between static strength at a given conventional low number of…
This is the second part of a short three-paper series, aiming to revisit some classical concepts of Linear Elastic Fracture Mechanics. Being the intermediate step of the analysis between infinite domains (discussed in Part-I) and finite…
This work deals with the notch sensitivity of sharp notches under multi-axial fatigue loading. The main discussion concerns the differences in notch sensitivity at high cycle fatigue regime, between tensile, torsional and combined loading.…
This paper presents a simple experimental procedure that greatly facilitates the use of digital image correlation (DIC) techniques in fatigue test conducted in resonant testing machines, without the need of test interruptions. This is…
Modified version of the crack compliance method is used for determination of stress intensity factor (SIF) related to narrow notches emanating from cold-expanded holes. These notches are inserted at different stages of low-cycle fatigue…
The contribution describes the fatigue lifetime predictions of polyethylene notched specimens based on the theory of critical distance. The approach uses the line method, which averages the axial stress over the critical distance. The…
Cracks at notches deserve special consideration in the design of steam turbine components. This work is addressed to investigate the crack initiation behavior a 10%Cr rotor steel with the help of notched specimens under service-type…
The theory of critical distances (TCD) has been applied to predict notch-based fracture and fatigue in a wide range of materials and components. The present paper describes a series of projects in which we applied this approach to human…
The novel destructive method is implemented for quantitative assessment of fatigue damage accumulation in the stress concentration zone accompanied by residual stress due to cold expansion of the through-thickness hole. Damage accumulation…
In the last decades the necessity of implant devices is continuously increasing. The researchers have thus focused their attentions on the development of new biocompatible materials, in particular polymers. Among them, polyetheretherketone…
The study focuses on examining the impact of internal manufacturing defects (voids and wrinkles) on the mechanical behavior of structural carbon fiber reinforced polymers (CFRP) under shear loading. Specimens of VKU/VSE1212 material with a…
The objective of this work is to analyze some geometrical effect to predict the damage of aluminum 2024T3 structure after validate numerical model by experimental test. The mechanical of damage behaviour under tensile tests of several…
The role of some geometrical characteristics of the notches machined in circular discs, in order to determine the mode-I fracture toughness of brittle materials, is discussed. The study is implemented both analytically and numerically.…
The purpose of this study is to devise a bending fatigue strength evaluation method that can be widely used for any machine component under the consideration that bending fatigue breakage depends on the initiation of a surface fatigue…
The present paper addresses experimentally the high temperature fatigue of 40CrMoV13.9 steel and the effect of surface roughness on fatigue strength and crack initiation. The 40CrMoV13.9 steel is widely used in different engineering high…
The near surface mounted (NSM) method of inserting fiber reinforced polymer (FRP) elements (rods or lamina) into notches has been shown to be a good way for restoring reinforced concrete (RC) elements. The knowledge about the use of…
The paper presents a result of experimental tests of welded S355 specimens subjected to combined bending and torsion loading. In order to analyse how the fillet joints’ shape and the load ratio affect the crack growth, we selected two…
Experimental method for a characterization of high-cycle fatigue evolution of residual stress near cold-expanded hole is developed and implemented. The technique is based on simultaneous measurements of deformation response to narrow…
This is the first part of a short three-paper series, aiming to revisit some classical concepts of Linear Elastic Fracture Mechanics. The motive of this first paper is to highlight some controversial issues, related to the unnatural…
In the last years, a large amount of fatigue test results from plain and bluntly notched specimens made of AISI 304L stainless steel were synthetized in a single scatter band by adopting the specific heat loss per cycle (Q) as a damage…
This paper is concerned with the fracture of composite materials containing stress concentration features such as notches and holes. In particular, it addresses the question of the use of the Theory of Critical Distances (TCD) – a method…
Localized displacement measurements based on electronic speckle-pattern interferometry are used to obtain crack mouth opening displacement (CMOD), stress intensity factor (SIF) and T-stress values during crack growth around cold-expanded…
An experimental investigation of the mechanical and fracture characteristics of Portland limestone and Corsehill sandstone is undertaken, aiming at enhancing understanding of the structural behaviour of these natural building stones…
In the present paper, the approach based on the strain energy density (SED) averaged over a structural volume is reformulated to estimate the lifetime of notched components subjected to variable amplitude (VA) uniaxial fatigue loading. The…