Abstract
The present paper addresses experimentally the high temperature fatigue of 40CrMoV13.9 steel and
the effect of surface roughness on fatigue strength and crack initiation.
The 40CrMoV13.9 steel is widely used in different engineering high temperature applications among which hotrolling of metals, where, in order to assure a constant temperature, the rolls are provided with cooling channels. These are the most stressed zone of the rolls where cracks systematically initiate. In order to completely characterize the high temperature behaviour of this steel, firstly uniaxial-tension load controlled fatigue tests have been conducted at different temperatures up to 650°C. Two geometries are considered: plain specimens and plates weakened by symmetric V-notches. Subsequently, with the aim to investigate the influence of the cooling channels roughness on the high temperature behaviour and the cracks initiation, uniaxial-tension load controlled fatigue tests have been conducted on plate with central hole at the service temperature of 650°C varying the surface roughness. After a brief review of the recent literature, the experimental procedure is described in detail and the new data from un-notched and notched specimens are summarized in terms of stress range, at the considered temperatures.
Finally, fatigue data from un-notched and notched specimens are re-analysed by means of the mean value of the Strain Energy Density (SED) approach extended at high temperature.
Keywords
Article history
- ReceivedUntil the next stage: 0 days
- AcceptedUntil the next stage: 0 days
- Published
How to cite
APA
IEEE
MLA
Chicago
Harvard
Vancouver
BibTeX
RIS
Licence
May be shared and adapted, provided appropriate credit is given. Copyright © 2015 Fracture and Structural Integrity.
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Fracture and Structural Integrity (F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit, providing a link to the license, and indicating if changes were made.
Similar articles
Most read articles by the same author(s)
- F. Berto, S.M.J. Razavi, J. Torgersen, Frontiers of fracture and fatigue: Some recent applications of the local strain energy density , Fracture and Structural Integrity: Vol 12 No 43 (2018): January 2018
- G. Meneghetti, A. Campagnolo, F. Berto, Some relationships between the peak stresses and the local strain energy density for cracks subjected to mixed-mode (I+II) loading , Fracture and Structural Integrity: Vol 9 No 33 (2015): July 2015
- M.R.M. Aliha, M. Fakhri, E. Haghighat Kharrazi, F. Berto, The effect of loading rate on fracture energy of asphalt mixture at intermediate temperatures and under different loading modes , Fracture and Structural Integrity: Vol 12 No 43 (2018): January 2018
- A. Campagnolo, F. Berto, L. P. Pook, Three-dimensional effects on cracked discs and plates under nominal Mode III loading , Fracture and Structural Integrity: Vol 9 No 34 (2015): October 2015
- G. Meneghetti, B. Atzori, A. Campagnolo, F. Berto, A link between the peak stresses and the averaged strain energy density for cracks under mixed-mode (I+II) loading , Fracture and Structural Integrity: Vol 9 No 34 (2015): October 2015
- P. J. Huffman, J. Ferreira, J.A.F.O. Correia, A.M.P. De Jesus, G. Lesiuk, F. Berto, A. Fernandez-Canteli, G. Glinka, Fatigue crack propagation prediction of a pressure vessel mild steel based on a strain energy density model , Fracture and Structural Integrity: Vol 11 No 42 (2017): October 2017
- F. Berto, Local approaches for the fracture assessment of notched components: the research work developed by Professor Paolo Lazzarin , Fracture and Structural Integrity: Vol 9 No 34 (2015): October 2015
- P. Lazzarin, M. Zappalorto, F. Berto, Recent developments in multi-parametric three-dimensional stress field representation in plates weakened by cracks and notches , Fracture and Structural Integrity: Vol 7 No 25 (2013): July 2013
- M.V. Karuskevich, S.R. Ignatovich, T.P. Maslak, A. Menou, P.?. Maruschak, S.V. Panin, F. Berto, Multi-purpose fatigue sensor. Part 2. Physical backgrounds for damages accumulation and parameters of their assessment , Fracture and Structural Integrity: Vol 10 No 38 (2016): October 2016
- F. Berto, M.R. Ayatollahi, S. Vantadori, A. Carpinteri, Review of the Influence of non-singular higher order terms on the stress field of thin welded lap joints and small inclined cracks in plates , Fracture and Structural Integrity: Vol 11 No 41 (2017): July 2017