This study aims at providing a better understanding of the effects of both microstructure and defect on the high cycle fatigue behavior of metallic alloys using finite element simulations of polycrystalline aggregates. It is well known…
In this paper the fatigue behaviour of a stainless steel AISI 304L is analysed. In the first part of the work the results obtained under constant amplitude fatigue are presented and synthesised in terms of both stress amplitude and energy…
In the present paper, mathematical models are proposed in order to analyze the strength of pinloaded lugs with semi-elliptical crack and through-the-thickness crack. The crack growth investigation of considered crack configurations tackles…
Crack initiation characteristics and fatigue property of a high-strength steel in very-high-cycle fatigue (VHCF) regime under different stress ratios were investigated in this paper. Fatigue tests were performed at stress ratios of -1…
The present report presents a fatigue life prediction method for large roller bearings applied in the turret turn table for large loading buoy units. The contact points between wheel and rail in these bearings are subjected to a…
The aim of this work is a review of scientific results in the literature, related to the application of thermographic techniques to composite materials. Thermography is the analysis of the surface temperature of a body by infrared rays…
The paper presents the results of experimental test of the fatigue of aluminium alloy type AlZn6Mg0,8Zr exposed to various low temperature thermomechanical treatment. Basquin’s characteristics of fatigue have been determined in mechanical…
Fatigue (high- and gigacycle) crack initiation and its propagation in titanium alloys with coarse and fine grain structure are studied by fractography analysis of fracture surface. Fractured specimens were analyzed by interferometer…
Orthotropic decks were applied to the long span bridges after World War II due to several advantages, such as light weight, high strength, few deck joints, durability, rapid construction, life-cycle economy. The fatigue problem of…
In this paper, a fatigue strength analysis approach based on Goodman-Smith fatigue limit diagram （GSFLD） and reliability theory is proposed to solve the problem that the traditional fatigue strength analysis of bogie frame is too…
The purpose of this study is to devise a bending fatigue strength evaluation method that can be widely used for any machine component under the consideration that bending fatigue breakage depends on the initiation of a surface fatigue…
For multiaxially-loaded parts several stress-based fatigue assessment concepts are applicable mostly taking uniaxial test results as basis. These approaches work well in case of proportional loading states, but on contrary, for…
The aim of the present paper is to systematically investigate the accuracy of the so-called Modified Wöhler Curve Method (MWCM) in estimating high-cycle fatigue strength of plain and notched engineering materials damaged by in-service…
The aim of the present research is to check the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating the fatigue strength of friction stir (FS) welded tubular joints of Al 6082-T6 subjected to in-phase and out-of-phase…
Plastics belong to the most complex and probably least understood engineering materials of today. Combining the best aspects of design, mechanical properties and manufacturing, the structural integrity of plastics is on par with aluminium…
In this work two different titanium dental implants are analyzed in order to evaluate their mechanical strength. An ad-hoc designed experimental apparatus is prepared to test against fatigue these implants in a way that approximates as…
Due to the abundance of engineering components subjected to complex multiaxial loading histories, being able to accurately estimate fatigue damage under multiaxial stress states is a fundamental step in many fatigue life analyses. In this…
The goal of the authors’ investigations was determination of the fatigue crack growth in fragments of steel structures (of the puddled steel) and its cyclic behavior. Tested steel elements coming from the turn of the 19th and 20th were…
This study concerns the multiaxial static and fatigue strength properties. Short-glass-fibre-reinforced phenolic-resin composites (SGP) molded by injection and compression processes were subjected to tensiontorsion combined static and…
The objective of this work is to evaluate the effects of mean stress on the fatigue behavior of ASTM A743 CA6NM alloy steel. It is used in several hydrogenator turbine components. In order to achieve it, 33 specimens were experimentally…
The modified Carpinteri-Spagnoli (C-S) criterion is a multiaxial high-cycle fatigue criterion based on the critical plane approach. According to such a criterion, the orientation of the critical plane is linked to both the averaged…
The investigation of fatigue strength of lotus-type structure with nodular cast iron as a base material using computational model is analysed in present study. The irregular pores distribution in transversal and longitudinal direction…
The present study aims to develop an algorithm able to predict the fatigue lifetime of nitrided steels. Linear multi-axial fatigue criteria are used to take into account the gradients of mechanical properties provided by the nitriding…
The torsional fatigue behaviour of circumferentially notched specimens made of austenitic stainless steel, SUS316L, and carbon steel, SGV410, characterized by different notch root radii has been recently investigated by Tanaka. In that…
The main purpose of this paper is to examine the influence of the critical plane orientation on the estimated fatigue strength of metals under multiaxial loading. The algorithm employed to evaluate fatigue strength implements the criterion…
In this work, the mechanical properties of Waspaloy superalloy have been evaluated in case of welded repaired material and compared to base material. Test program considered flat specimens on base and TIG welded material subjected to…
This article deals with the locally multiaxial fatigue behaviour of high strength steel. To this end, the influence of the cracking path deflections (at the micro level) on the plasticity-induced fatigue crack growth is analyzed. With…
Titanium alloy (Ti-6Al-4V) having a bimodal “harmonic structure”, which consists of coarsegrained structure surrounded by a network structure of fine grains, was fabricated by mechanical milling (MM) and spark plasma sintering (SPS) to…
This work deals with the notch sensitivity of sharp notches under multi-axial fatigue loading. The main discussion concerns the differences in notch sensitivity at high cycle fatigue regime, between tensile, torsional and combined loading.…
A356-T6 cast aluminum alloy is a light weight structural material, but fatigue crack initiates and propagates from a casting defect leading to final fracture. Thus it is important to eliminate casting defects. In this study, friction stir…
Mounting stiffness has an important impact on a system’s structural dynamics and also on the durability of many structures. Mounts with tunable stiffness allow adapting a system’s structural dynamic behavior. Furthermore, they can be used…
The objective of the present paper is to clarify the effect of defect length in depth direction on rolling contact fatigue (RCF) crack propagation in high strength steel. RCF test and synchrotron radiation micro computed tomography (SR…
Ultrasonic impact treatment (UIT) is a remarkable post-weld technique applying mechanical impacts in combination with ultrasound into the welded joints. In the present work, a 3D simulation method including welding simulation, numerical…
Dealing with composites in polymeric matrix, the pultruded ones are among the more suitable for large production rates and volumes. For this reason, their use is increasing also in structural applications in civil and mechanical…
Tensile and stress controlled fatigue tests were performed to investigate the influence of forging at a temperature of 400°C at different rates, on the performance of extruded AZ31B magnesium alloy. The obtained microstructural analysis…
The influence of forging conditions on the propagation of physically small fatigue cracks has been studied for two high strength steels. Two surface conditions were produced after the forging process. The subsurface microstructure of the…
The fatigue behaviour of circumferentially notched specimens made of titanium alloy, Ti-6Al-4V, has been analysed. To investigate the notch effect on the fatigue strength, pure bending, pure torsion and multiaxial bending-torsion fatigue…
This paper presents results of experimental examinations of stress concentration influence to fatigue life of butt welded joints with K-groove, produced from the most frequently used structural steel S355J2+N. One group of experiments…
While it is well known that fatigue crack growth in metals that display confined slip, such as high strength aluminium alloys, develop crack paths that are responsive to the loading direction and the local microstructural orientation, it…
This work presents an in-depth study of the low-cycle fatigue behaviour of ferritic-pearlitic HSLA-420 high-strength steel sheets, with emphasis on the influence of loading direction on fatigue life and damage mechanisms. Plastic…
Multiaxial fatigue failure criteria are formulated in time and frequency domain. The number of frequency domain criteria is rather small and the most popular one is the equivalent von Mises stress criterion. This criterion was elaborated…
Different alloys can be used for Additive Manufacturing (AM) with good structural strength. Among the titanium alloys, Ti6Al4V is the most used, especially for aerospace applications. There have been many analyses of the mechanical…
Ultra-high-strength steels (with tensile strength higher than 980 MPa) are widely used in automobile manufacturing owing to their lightweight that contributes to fuel efficiency. The fatigue strength of ultra-high-strength steels with a…
The present study investigates the influence of corrosion exposure on the fatigue behavior of S460NL high-strength structural steel, a material that is frequently utilized in offshore and civil engineering structures. Accelerated corrosion…
A new fatigue testing device has been developed to test specimens under biaxial loading at 20 kHz. A flat smooth specimen with a disc geometry is placed on a torus frame and cyclically loaded at the center of its upper face. Disc bending…
The quickly identify of fatigue limit of a mechanical component with good approximation is currently a significant practical problem not yet resolved in a satisfactory way. Generally, for a mechanical component, the fatigue strength…
The present paper is concerned with the formulation of an elasto-plastic strain based approach suitable for assessing fatigue strength of notched components subjected to in-service variable amplitude cyclic loading. The hypothesis is…
Two implicit progressive fatigue damage models that rely on new equivalent-damage and equivalent-stress criteria are presented for the prediction of various failure modes of the composites. The criteria are coupled with lamina-based and…
In fatigue life, surface integrity perform a major role to determine the fatigue lifetime. It could differ greatly among specific cases even for the same solicitations. Indeed, the manufacturing process carries modifications on surface…
This paper explores the effect of internal technological defects on the fatigue life of carbon fiber reinforced plastic (CFRP) under simple loading waveforms. One conducted experiments on CFRP specimens with embedded artificial defects…