The influence of the non-proportional loadings on the fatigue life depends on the material ductility. Ductile materials react with a shortening of lifetime compared to proportional loading conditions. For a semiductile material there is…
The contribution describes the fatigue lifetime predictions of polyethylene notched specimens based on the theory of critical distance. The approach uses the line method, which averages the axial stress over the critical distance. The…
Research on determining the lifetime of an expansion bellows designed to compensate the difference in expansion between the shell and the tubes in a fixed tube sheet heat exchanger has never ceased because of its Importance in a heat…
The structures of the hydraulic excavator and the crane have numerous one-sided welded joints. However, attachments with box like structures are difficult to weld at both sides. Therefore, high accurate evaluation method is needed. In this…
This paper initially investigates the accuracy of two methods, i.e., the Maximum Variance Method (MVM) and the Maximum Damage Method (MDM), in predicting the orientation of the crack initiation plane in three different metallic materials…
The structures of the hydraulic excavator and the crane have numerous one-sided welded joints. However, attachments with box like structures are difficult to weld at both sides. Therefore, high accurate evaluation method is needed. In this…
This study based on a new fracture mechanics parameter is concerned with assessing the integrity of cracked steam turbine disk which operate under startup-shutdown cyclic loading conditions. Damage accumulation and growth in service have…
This article presents the bending fatigue behavior and the scatter-band analysis of aluminum alloys under beneficial conditions of nano-clay-particles and heat-treating, compared to detrimental conditions of the mechanical stress and the…
Cold expansion by hardening is a common process used in the aerospace industry to extend the fatigue lifetime of assembly holes, through a field of high compressive tangential residual stresses. The understanding and the control of the…
The present paper is concerned with the formulation of an elasto-plastic strain based approach suitable for assessing fatigue strength of notched components subjected to in-service variable amplitude cyclic loading. The hypothesis is…
Nowadays lifetime calculation in the high cycle fatigue region is commonly based on S/N curves which are modified by different influences to ensure accurate results. Especially the application of these models is important when small…
The present study aims to develop an algorithm able to predict the fatigue lifetime of nitrided steels. Linear multi-axial fatigue criteria are used to take into account the gradients of mechanical properties provided by the nitriding…
Cracks at notches deserve special consideration in the design of steam turbine components. This work is addressed to investigate the crack initiation behavior a 10%Cr rotor steel with the help of notched specimens under service-type…
A new critical plane approach based on the modified Manson-Coffin curve method (MMCCM) is presented in this paper for predicting fatigue lifetime under variable amplitude (VA) multiaxial fatigue loading. The critical plane is assumed to…
The current energy policy envisages extended lifetime for the current nuclear power plants (GEN II NPP). This policy imposes a large research effort to understand the ageing of power plant components. In this goal, it is necessary to…
Various input variables, including corrosion time, fretting force, stress, lubrication, heat-treating, and nano-particles, were evaluated by modeling of stress-controlled fatigue lifetimes in AlSi12CuNiMg aluminum alloy of the engine…
The structural integrity and reliability of glass components are key issues for concentrated solar power (CSP) systems. For example, the glass windows in a solar furnace may suffer catastrophic fracture due to thermal and structural…
In the present paper, the multiaxial fatigue life assessment of notched structural components is performed by employing a strain-based multiaxial fatigue criterion. Such a criterion, depending on the critical plane concept, is extended by…
Fretting fatigue experiments aim to represent industrial problems and most of them endure variable loading. Being able to assess lifetime of assemblies, especially for low propagation rate conditions, is essential as experimental…
The present paper investigates the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating multiaxial fatigue strength of aluminium friction stir (FS) welded joints. Having developed a bespoke joining technology…
The Miner number M, used as a tool for lifetime prediction of mechanical and structural components in most of the standards related to fatigue design, is generally accepted as representing a damage stage resulting from a linear progression…
This paper gives a highlight about pressure vessel (PV) methods of design to initiate new engineers and new researchers to understand the basics and to have a summary about the knowhow of PV design. This understanding will contribute to…
Fatigue lifetime assessment is essential in the design of structures. Under-estimated predictions may result in unnecessary in service inspections. Conversely, over-estimated predictions may have serious consequences on the integrity of…
Additive Manufacturing (AM) is a new innovative technique that allows the direct fabrication of complex, individual, delicate and high-strength products, based on their 3D data. Selective Laser Melting (SLM) is one of the AM processes that…
Marine structures are particularly prone to action of waves, winds and currents with stochastically varying composition, intensities and directions. Therefore, resultant stresses may cause multiaxial fatigue in specific welded structural…
In this paper we investigated the influence of consecutive dynamic and gigacycle fatigue loads on the lifetime of aluminum-magnesium alloy AlMg6. Preloading of samples was achieved during dynamic tensile tests in the split-Hopkinson bar…
Buildings, structures and systems of large scale and high value (e.g. conventional and nuclear power plants, etc.) are designed for a certain, limited service lifetime. If the standards and guidelines of the time are taken into account…
The objective of the present paper is to investigate the stress-controlled low-cycle fatigue behavior of piston aluminum-silicon (AlSi) alloy reinforced with nano-clay particles and T6 heat-treatment. The piston aluminum-silicon alloy…
The reliability of printed circuit boards under dynamic loads is a key issue in the handheld electronic products industry. In order to predict the performance of the boards in their application lifetime, different tests were developed. The…
In the present paper, the approach based on the strain energy density (SED) averaged over a structural volume is reformulated to estimate the lifetime of notched components subjected to variable amplitude (VA) uniaxial fatigue loading. The…
Isotactic polybutene-1 (i-PB1) is a polymer used for the manufacturing of pressurized pipes. In this work two grades of i-PB1 with a different degree of isotacticity have been investigated; they have been supplied by Basell Polyolefins.…
The work is devoted to experimental investigation of the laser shock peening (LSP) effect on fatigue crack propagation rate and heat dissipation at the crack tip in specimens made of titanium alloy Grade 2 with a stress concentrator. It is…
Polymers are known to be sensitive to aging; their lifetime can be predicted through experimental tests. The present paper presents an experimental study on the long-term performance of polymethyl methacrylate (PMMA) exposed to solar and…
The novel destructive method is implemented for quantitative assessment of fatigue damage accumulation in the stress concentration zone accompanied by residual stress due to cold expansion of the through-thickness hole. Damage accumulation…
Nodular cast iron (GJS) represents one of the most widely used materials for vehicle, energy and heavy machinery industry. Nevertheless, foundries struggling with the influence of local material defects in GJS like pores, shrinkages and…
In this investigation, fatigue criterion was established to predict crack-initiation at the tip of a notch in aged hardening aluminum alloy. This criterion was used to predict the residual lifetime in aeronautical structures using concept…
The work reports the observed fatigue damage of C45 steel specimens tested in a previous work under multiaxial loading conditions and its relationship with the thermal energy dissipation which has been used in the last decades to estimate…
Different structural and machine elements are used over the ages. These are subjected to various loads like static and dynamic load, temperature, corrosion etc. Due to the above-mentioned reasons, ageing of the structural elements occur.…
Ageing infrastructure is of major concern for different industrial sectors across Europe. Fatigue cracking is one of the most important damage mechanisms that affect structural health of welded steel structures. Fatigue assessment of…
The availability of engineering strength data on shape memory alloys (SMAs) under cyclic thermal activation (functional fatigue) is central to the rational design of smart actuators based on these materials. Test results on SMAs under…
CPVC is an increasingly popular material for plumbing pipes and other applications that require strong and temperature-resistant material. This resin is created using a chlorination process, giving it Chlorine levels that range from 63 to…
In fatigue life, surface integrity perform a major role to determine the fatigue lifetime. It could differ greatly among specific cases even for the same solicitations. Indeed, the manufacturing process carries modifications on surface…
The oxidation resistance of iron-based alloys depends on the formation of thin protective films consisting ofreaction products between the alloys and the ambient atmosphere. The high corrosion resistance of Fe-Cr-Mo alloys hasbeen…
Due to the substantial need to continuously ensure safe excavations and sustainable operation of deep engineering structures, structural health monitoring based on remote sensing techniques has become a prominent research topic in this…
This study presents a hybrid framework integrating a physics-based corrosion model with a feedforward neural network (FNN) to predict corrosion rates and estimate the remaining useful life (RUL) of industrial pressure vessels for…
Abstract. In this article, the effect of nano-clay particles and heat-treating on thermo-mechanical fatigue (TMF) behaviors and failures of piston aluminum-silicon (AlSi) alloys was investigated. For this purpose, thermo-mechanical fatigue…
Modified version of the crack compliance method is used for determination of stress intensity factor (SIF) related to narrow notches emanating from cold-expanded holes. These notches are inserted at different stages of low-cycle fatigue…