The main objective of the work is to study the fracture behavior of AA6061-graphite material using both experimental technique and finite element simulation by considering helicopter rotor blade as a case study. From the case study, it has…
This paper presents a numerical method for non-local stress assessment by means of a general FE tool and the local stress field. Unlike usual calculations by means of a numerical PDE solver, a more general numerical integration is used.…
Fatigue cracking of longerons manufactured from Al-alloy AVT-1 for helicopter in-service rotor-blades was considered and crack growth period and equivalent of tensile stress for different blade sections were estimated. Complicated case of…
This paper is focused on delamination fracture analyses of a multilayered functionally graded circular shaft under two loading combinations (centric tension and torsion, and bending and torsion) assuming non-linear elastic mechanical…
The present paper investigates the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating multiaxial fatigue strength of aluminium friction stir (FS) welded joints. Having developed a bespoke joining technology…
The aim of this work is to investigate stress gradient effects on the fatigue life estimation of notched Al 7050-T7451 specimens under combined torsion and push-pull loading conditions. Initially, simple push-pull and torsion fatigue tests…
This study concerns the multiaxial static and fatigue strength properties. Short-glass-fibre-reinforced phenolic-resin composites (SGP) molded by injection and compression processes were subjected to tensiontorsion combined static and…
An edge crack propagation in a steel bar of circular cross-section undergoing multiaxial fatigue loads is simulated by Finite Element Method (FEM). The variation of crack growth behaviour is studied under axial and combined in phase…
The objective of this research work is to study the fracture behavior of Al6061 with graphite particulate composite produced by the stir casting technique. For the study different composition of the particulate metal matrix composite used…
The aim of the paper was investigation crack initiation and fracture features developed during compression of Fe-based bulk metallic glass (BMG). These Fe-based BMG has received great attention as a new class of structural material due to…
The concept of ratchetting strain as a crack driving force in controlling crack growth has previously been explored at Portsmouth using numerical approaches for nickel-based superalloys. In this paper, we report the first experimental…
We analyse the problem of a simply supported steel beam subjected to uniformly distributed load, strengthened with a pre-stressed fibre-reinforced polymer (FRP) laminate. We assume that the laminate is first put into tension, then bonded…
Near tip full-field strains in a growing fatigue crack have been studied in situ using the Digital Image Correlation (DIC) technique in a compact tension specimen of stainless steel 316L under tension-tension cyclic loading. An error…
Fatigue surface crack growth is studied through experiments and computations for aluminum alloys D16T and B95AT (analogue of 2024 and 7075 aluminum). Subjects for studies are cylindrical hollow specimens with external semi-elliptical…
For multiaxially-loaded parts several stress-based fatigue assessment concepts are applicable mostly taking uniaxial test results as basis. These approaches work well in case of proportional loading states, but on contrary, for…
This paper for the first time presents an equation for calculating the mechanical fracture energy of the polymeric composite material (PCM) with regard to the basic formulation parameters. By means of the developed computer program the…
Rebar corrosion significantly affects the overall performance and the service life of reinforced concrete (RC) structures due to the reduction in the bond strength between concrete and rebar, leading to the delamination of the concrete…
By means of numerical experiment the authors investigate dependence of conventional rupturing stress and mechanical fracture energy at uniaxial tension from fractional composition of dispersed filler, plasticizer volume fraction in polymer…
This paper deals with the fatigue crack propagation behavior of rolled AZ31B magnesium alloy (grain size: approximately 40 ?m). Fatigue crack propagation tests were performed on single edge notched tension specimens at a stress ratio of R…
The work deals with experimental study of macro localization of plastic yielding occurrences of structural carbon steel, research of singularity of deformation wave processes by complex use of contemporary test equipment and high effective…
For various configurations examined in a series of fatigue experiments on thin-walled tubes under tension and torsion, the experimental results – crack path, crack growth life, near crack tip deformations, and crack closure – are measured…
The mechanical and nanomechanical properties of multi-walled carbon nanotube-reinforced polypropylene (MWCNT/PP) nanocomposite were investigated through tension tests (conducted on 2 wt% and 5 wt% specimens) and nanoindentation tests…
A 3D mixed beam finite element is presented, modeling the warping of the cross-sections as an independent kinematic field. The beam formulation is derived on the basis of the Hu-Washizu variational principle, expressed as function of four…
The present paper addresses experimentally the high temperature fatigue of 40CrMoV13.9 steel and the effect of surface roughness on fatigue strength and crack initiation. The 40CrMoV13.9 steel is widely used in different engineering high…
An experimental technique is presented to evaluate mechanical and thermal load-induced microstructural damage, based on the Electron Probe Micro-Analysis (EPMA) principle, by which certain analytical potentialities of Scanning Electron…
A study on the approximation of the stress field in the vicinity of crack tip in a compact tension specimen made from Al 2024-T351 is presented. Crack tip stress tensor components are expressed using the linear elastic fracture mechanics…
Nowadays, fibre-reinforced composite materials are widely used in many fields, e.g. automotive and aerospace. Natural fibres such as flax and hemp provide good density specific mechanical properties. Additionally, the embodied production…
The paper is devoted to theoretical and experimental investigation of materials behavior on postcritical deformation stage (strain softening). Tests results, which confirm theoretical justification of specimen configuration impact on the…
The paper describes the key principles and results of preliminary experiments aimed at the development of new technique for the fatigue life prediction under conditions of biaxial cyclic tension. The foundations of the method were…
In this work, a link between the averaged strain energy density (SED) approach and the peak stress method in the case of cracks subjected to mixed mode (I+II) loading has been investigated. Some closed-form expressions of the strain energy…
In the case of quasi-brittle material, there is a zone of non-linear behaving material, near the crack tip. A major part of this zone forms a socalled fracture process zone (FPZ), where mechanisms of material toughening take place. The…
In this study, experimental and numerical results of compact tension shear (CTS) specimen and a new specimen type under in-plane mixed mode (Mode-I/II) loading conditions are compared with existing inplane mixed mode fracture criteria to…
In the present work, the damage propagation of a masonry arch induced by slow cyclic and dynamic loadings is studied. A two-dimensional model of the arch is proposed. A nonlocal damage-plastic constitutive law is adopted to reproduce the…
In this paper the fatigue crack growth tests were carried out on surface-crack tension (SCT) specimens, made of 7050 and Ti6Al4V alloys, with initial semi-elliptical surface cracks. Pure Mode I conditions were realized on SCT specimens…
This work is motivated by the increasing interest towards the application of the “Projection-by-Projection” (PbP) spectral method in finite element (FE) analysis of components under multiaxial random loadings. To help users and engineers…
In this paper, the macro and micro-mechanical fracture behavior was studied for aluminum (Al6061) alloy matrix, reinforced with various proportions of TiC particles such as 3wt%, 5wt% and 7wt%. The Al6061-TiC metal matrix composites were…
This work deals with the notch sensitivity of sharp notches under multi-axial fatigue loading. The main discussion concerns the differences in notch sensitivity at high cycle fatigue regime, between tensile, torsional and combined loading.…
This paper focusses on discussing equivalent stress intensity factors and kink angles after a change of mode-mixity from one cycle to the next and when the mode-mixity changes continuously during the fatigue cycles. Thin-walled tubes with…
Fatigue tests run-out specimens up to 106 – 5x107 load cycles are used to determine the stress level named “fatigue limit”. Nevertheless, it is not clear what kind of fatigue cracking takes or will take place in these specimens. To discuss…
Multiaxial fatigue failure criteria are formulated in time and frequency domain. The number of frequency domain criteria is rather small and the most popular one is the equivalent von Mises stress criterion. This criterion was elaborated…
The paper studies the processes of deformation and fracture in nanocomposites. The study was curry out by the method of mathematical modeling. The behavior of the nanosystem was described by the molecular dynamics apparatus. A modified…
The paper studies the adhesive strength of aluminum alloy specimens bonded with the use of an epoxy adhesive, under the tensile-shear stress state, depending on the testing temperature. Tension of modified Arcan specimens with load angles…
The deformation behaviour and fracture mechanisms of high-density polyethylene (HDPE), polypropylene (PP) and polyamide 6 (PA 6) are investigated experimentally under different stress states and at different crosshead speeds of 1, 20 and…
The article presents the results of computational and experimental studies of the strength and damageability of a connecting composite part in a metal-composite joint of isogrid and anisogrid structures made of polymer composite material…
Polymers are known to be sensitive to aging; their lifetime can be predicted through experimental tests. The present paper presents an experimental study on the long-term performance of polymethyl methacrylate (PMMA) exposed to solar and…
This paper presents the development of the multiple linear regression approach based on the stress ratio and applied load that was assessed using entropy generation. The energy dissipation is associated with material degradation to…
This work describes a two-dimensional numerical model that allows detecting the appearance of cracks and calculating their propagation in elements made of laminated bamboo, under tension and shear. This composite material has long parallel…
The rapid development of inhomogeneous and anisotropic materials like carbon fiber reinforced polymers (CFRP) with epoxy matrices necessitates a multidisciplinary approach for safe use. This approach should integrate computational modeling…
The aim of this work is to solve the methodological issues of the experimental study of the nucleation and propagation of deformation bands due to the Portevin-Le Chatelier effect under conditions of complex loading. It is of interest to…
The work is devoted to the experimental study of mechanical behavior regularities of the structural steel 40Cr under postcritical deformation of specimens in conditions of strain localization formation in the form of neck during extension.…