Under the typical partial slip conditions under which fretting fatigue takes place, the amount of superficial damage is small. Therefore, the substantial reduction in fatigue life caused by fretting, when compared to plain fatigue, may…
This work deals with the notch sensitivity of sharp notches under multi-axial fatigue loading. The main discussion concerns the differences in notch sensitivity at high cycle fatigue regime, between tensile, torsional and combined loading.…
Cracking direction in multiaxial low cycle fatigue is an important research subject because crack initiation and propagation behavior is a physical background for developing an estimation method of multiaxial low cycle fatigue lives.…
The presence of notches and other stress concentrations in turbine blades and other notch hydraulic components is a current problem in engineering. It causes a reduction of endurance limit of material. In that sense, specimens of the ASTM…
Semi–empirical notch sensitivity factors q have been widely used to properly account for notch effects in fatigue design for a long time. However, the intrinsically empirical nature of this old concept can be avoided by modeling it using…
The torsional fatigue behaviour of circumferentially notched specimens made of austenitic stainless steel, SUS316L, and carbon steel, SGV410, characterized by different notch root radii has been recently investigated by Tanaka. In that…
The present paper describes a novel experimental technique recently presented that allows one to study interactions between the crack and microstructural barriers with an unprecedented level of ease and detail. The method consists in…
The behavior of short cracks that depart from elastoplastic notch tips is modeled to estimate the stresses required to initiate and to propagate cracks in notched structural components, and to evaluate the size of tolerable crack-like…
For multiaxially-loaded parts several stress-based fatigue assessment concepts are applicable mostly taking uniaxial test results as basis. These approaches work well in case of proportional loading states, but on contrary, for…
The fatigue behaviour of circumferentially notched specimens made of titanium alloy, Ti-6Al-4V, has been analysed. To investigate the notch effect on the fatigue strength, pure bending, pure torsion and multiaxial bending-torsion fatigue…
To meet the design requirements, different types of defects are often machined on the surface of fatigue components. Local stress concentration formed at the notch accelerate the initiation of fatigue crack, therefore greatly shorten the…
In the present paper, the multiaxial fatigue life assessment of notched structural components is performed by employing a strain-based multiaxial fatigue criterion. Such a criterion, depending on the critical plane concept, is extended by…
This paper presents results of experimental examinations of stress concentration influence to fatigue life of butt welded joints with K-groove, produced from the most frequently used structural steel S355J2+N. One group of experiments…
The purpose of this study is to devise a bending fatigue strength evaluation method that can be widely used for any machine component under the consideration that bending fatigue breakage depends on the initiation of a surface fatigue…
The contribution describes the fatigue lifetime predictions of polyethylene notched specimens based on the theory of critical distance. The approach uses the line method, which averages the axial stress over the critical distance. The…
Weld start and end points are fatigue failure sensitive locations. Their fatigue behaviour especially in thin sheet structures under multiaxial load conditions is not sufficiently explored so far. Therefore, a research project was…
High resolution synchrotron X-ray tomography has been used to obtain 3D images of arrested cracks initiated at small artificial defects located on the surface of cylindrical steel specimens subjected to mode I fatigue loading. These…
The present paper investigates the multiaxial fatigue strength of sharp V-notched components made of titanium grade 5 alloy (Ti-6Al-4V). Axisymmetric notched specimens have been tested under combined tension and torsion fatigue loadings…
Ultra-high-strength steels (with tensile strength higher than 980 MPa) are widely used in automobile manufacturing owing to their lightweight that contributes to fuel efficiency. The fatigue strength of ultra-high-strength steels with a…
While a long stable crack propagation phase was observed during experiments of complex welded components, very conservative assessments of the fatigue life were achieved in the past. The difference was explained by the stress gradient…
As often done in design practice, the Wöhler curve of a specimen, in the absence of more direct information, can be crudely retrieved by interpolating with a power-law curve between static strength at a given conventional low number of…
A large number of mechanical components are subjected to fatigue loading beyond 106 cycles. The VHCF behaviour of smooth specimens has been extensively investigated in the recent years, even if more efforts are necessary to reveal the…
The present paper is concerned with the formulation of an elasto-plastic strain based approach suitable for assessing fatigue strength of notched components subjected to in-service variable amplitude cyclic loading. The hypothesis is…
The purpose of this work is to validate the N-SIF, SED and ENS approaches for the fatigue design of austenitic stainless steel welded joints. Literature fatigue data for cruciform welded joints, originally expressed in terms of nominal…
The exhaustion of constructive ways for increasing the service life of parts has led to the development of new methods which can improve their material properties during operation under various loading conditions. Laser shock peening (LSP)…
Mechanical components fabbricated with quenched and tempered steels, exhibiting mixed microstructures as derived from slant quench conditions, are frequently encountered in the industrial practice, owing to a tendency to employ quite low…
A series of strain-controlled multiaxial low cycle fatigue (LCF) tests under proportional and non-proportional loading conditions have been conducted on notched specimens. Cylindrical bars of Al 6061 aluminum alloy and AISI 316L stainless…
The novel destructive method is implemented for quantitative assessment of fatigue damage accumulation in the stress concentration zone accompanied by residual stress due to cold expansion of the through-thickness hole. Damage accumulation…
In this research, the effect of thermally expandable microcapsules (TEMs) on mode I fracture toughness of structural adhesives were investigated. The single-edge-notch bending (SENB) test was used. Firstly, a standard toughness test was…
Europe has a number of ancient riveted metallic bridges, constructed during the second half of the 19th century up to the middle of the 20th century, which are still in operation. In this paper, a unified approach is presented to generate…
High cycle fatigue tests were conducted for stainless steel AISI 304L. The geometry was a thin walled tube with a passing through hole. The tests were axial, torsional and in-phase axial-torsional, all of them under load control with R =…
Many engineering structures are exposed to non-proportional fatigue loading. However, at the critical location of crack initiation, often only one of the load sequences dominates – the individual load cases result in different crack…
The present paper investigates the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating multiaxial fatigue strength of aluminium friction stir (FS) welded joints. Having developed a bespoke joining technology…
In the last decades the necessity of implant devices is continuously increasing. The researchers have thus focused their attentions on the development of new biocompatible materials, in particular polymers. Among them, polyetheretherketone…
Onyx ® is a new material composed of Polyamide 6 reinforced with short carbon fiber, used in the novel additive manufacturing composites technique. This paper aims to present the axial fatigue performance of this material with and without…
Gradient Elasticity (GE) allows the stress analysis to be performed by taking into account the size of the dominant source of microstructural heterogeneity via a suitable length scale parameter. This is done by simply assuming that the…
In this investigation, fatigue criterion was established to predict crack-initiation at the tip of a notch in aged hardening aluminum alloy. This criterion was used to predict the residual lifetime in aeronautical structures using concept…
Several methods can be used to estimate elastoplastic (EP) notchtip stresses and strains from linear elastic calculations, providing EP stress and strain concentration factors. For uniaxial load histories, Neuber’s and Glinka’s rules are…
The paper presents the results of tests on the fatigue crack growth for a constant moment amplitude under combined bending with torsion in the aluminium alloy AW-2017A-T4. The tests were performed under different values of the load ratio…
Notches and cracks are usually approximately modeled as two-dimensional problems using solutions from plane elasticity to quantify localized stress/strain concentration effects around their tips. However, they may be associated with high…
This work presents a novel methodology for characterising fatigue cracks under biaxial conditions. The methodology uses high magnification Digital Image Correlation (DIC) technique for measuring displacement and strain crack-tip fields. By…
The CJP model of crack tip stresses is a modified version of the Williams crack tip stress field which takes account of simplified stress distributions that arise from the presence of a zone of plastic deformation associated with the crack…
In the last years, a large amount of fatigue test results from plain and bluntly notched specimens made of AISI 304L stainless steel were synthetized in a single scatter band by adopting the specific heat loss per cycle (Q) as a damage…
Experimental method for a characterization of high-cycle fatigue evolution of residual stress near cold-expanded hole is developed and implemented. The technique is based on simultaneous measurements of deformation response to narrow…
The work is devoted to experimental study of heat flow evolution at the fatigue crack tip during biaxial loading. The plane samples of titanium alloy Graid-2 with thick of 1 mm were weakened by notch to initiate fatigue crack at the center…
This paper deals with the fatigue assessment of cast steel defects in terms of macroscopic shrinkage porosity. Within preliminary studies, a generalized Kitagawa diagram GKD was established by numerical analyses of V-notched specimens with…
In this paper, high cycle fatigue failure behavior of Load-carrying Cruciform Welded Joints (LCWJ) is assessed using Strain Energy Density (SED) approach. Different analytical solutions are proposed and applied to illustrate the effects of…
Cracks at notches deserve special consideration in the design of steam turbine components. This work is addressed to investigate the crack initiation behavior a 10%Cr rotor steel with the help of notched specimens under service-type…
Two cracks, initiated from the opposite tips of a central notch inclined by 45°, were considered in cruciform specimens made of Ti6246. A static load was applied to a cruciform arm while a cyclic load was applied along the other arm.…
Fatigue crack growth (FCG) is linked to irreversible and non-linear processes happening at the crack tip, which explains different problems observed in the use of da/dN-DK curves. The replacement of DK by non-linear crack tip parameters…