Aeroengine manufacturers have to demonstrate that critical components such as turbine disks, made of DA Inconel 718, meet the certification requirements in term of fatigue crack growth. In order to be more representative of the in service…
An inhomogeneous distribution of non-metallic inclusions can result from the steel casting process. The aim of the present study was to investigate the damaging effect of an inhomogeneous distribution of nonmetallic inclusions on the crack…
Crack initiation and propagation have been investigated on the polymeric material ABS (Acrylonitrile Butadiene Styrene), under ultrasonic fatigue testing. Three controlled actions were implemented in order to carry out fatigue tests at…
In recent years, mechanical property of many SMA has improved in order to introduce these alloys in specific field of industry. Main examples of these alloys are the NiTi, Cu-Zn-Al and Cu-Al-Ni which are used in many fields of engineering…
In this paper, the attention is paid to investigation of the importance of the interfacial transition zone (ITZ) in selected fine-grained cement-based composites for the global fracture behaviour. This is a region of cement paste around…
We propose the interpretation of the Finite Fracture Mechanics based on the criticality of damage-failure transition due to specific metastability of free energy release. Multiscale mechanisms of fatigue damage-failure transitions in…
Very-High-Cycle-Fatigue regime for metals was considered and mechanisms of the subsurface crack origination were introduced. In many metals first step of crack origination takes place with specific area formation because of material…
Simulating the concrete fracture unlike other elastic and brittle materials quite different due to its quasibrittleness. The present research focussed on assess softening behavior by varying different fractions of aggregates and cement…
According to Gradient Mechanics (GM), stress fields have to be determined by directly incorporating into the stress analysis a length scale which that takes into account the material microstructural features. This peculiar modus operandi…
Localized displacement measurements based on electronic speckle-pattern interferometry are used to obtain crack mouth opening displacement (CMOD), stress intensity factor (SIF) and T-stress values during crack growth around cold-expanded…
Shape memory property characterizes the behavior of many Ti based and Cu based alloys (SMAs). In Cu-Zn-Al SMAs, the original shape recovering is due to a bcc phase that is stable at high temperature. After an appropriate cooling process…
Part-through surface or corner 2D cracks are commonly found in structural components, even because practically all fatigue cracks tend to start this way. It is a reasonable hypothesis to model them assuming the shape of their fronts is…
The size effect significantly influences the structural design of concrete elements, particularly when applying fracture mechanics principles. As structural dimensions increase, a significant outcome of the size effect is the decline in…
In this study, an efficient computational method for modeling the transition from transgranular to intergranular fracture mechanisms based on phase field fracture theory is discussed. Structural heterogeneity of the material is modeled on…
The paper presents the results of experimental and theoretical investigations of the mechanisms of crack formation in reinforced concrete beams subjected to quasi-static bending. The boundary-value problem has been formulated in the…
Phase-field models have become a powerful tool to simulate crack propagation. They regularize the fracture discontinuity and smooth the transition between the intact and the damaged regions. Based on the thermodynamic function and a…
A present study reveals the influence of nano Al2O3 and ZrO2 reinforcements on the fracture toughness of Hybrid Metal matrix Composites (HMMCs) made of Al6061 alloy. Composites are synthesized by varying weight fraction of alumina and…
Experimental method for a characterization of high-cycle fatigue evolution of residual stress near cold-expanded hole is developed and implemented. The technique is based on simultaneous measurements of deformation response to narrow…