In the last decades, damaging micromechanisms in ductile cast irons (DCIs) have been widely investigated, considering both the matrix microstructure and the loading conditions influence. Considering the graphite nodules, they were…
In the cohesive framework, a stress-state dependent cohesive model, combined with an irreversible damage parameter has been used in simulation of fatigue crack growth initiation and continued growth. The model is implemented as interface…
Fatigue surface crack growth and the in-plane and out-of-plane constraint effects are studied through experiments and computations for aluminium alloy D16T. Subjects for studies are cruciform specimens under different biaxial loading and…
Epoxy resin reinforced with 10% of TiO2 and pure epoxy resin are taken to exemplify the possibility of constructing a fracture locus for engineering organic polymers as a dependence of ultimate strain energy density in cohesive failure on…
The reduced state of stress triaxiality observed in shallow cracked components allows an increased capacity to resist crack propagation compared to that observed in deeply cracked specimens. This may be regarded as a higher fracture…
This paper is devoted to the numerical and experimental study of ductile fracture in bulk metal forming of the 2017A-T4 aluminum alloy. From an experimental standpoint, the ductile fracture of the 2017A-T4 aluminum alloy is investigated…
The stress-strain state analysis of the gas turbine engine compressor disk was carried out taking into account damage accumulation under various loading conditions in the temperature range. Characterization of the constraint effects was…
To describe the effect of crack-tip constraint on the stress field for finite cracked bodies, the following most widely used constraint parameters can be employed in elastic-plastic fracture mechanics, namely, local triaxiality parameter…
The publication presents a cruciform specimen for the determination of cyclic crack growth data under biaxial loading. The design of the specimen with slotted loading arms allows good decoupling between the two loading directions. For…
The characterization of ductile damage evolution, and its description, have been the object of extensive research in the continuum damage mechanic field. Many different models have been developed since the pioneering works carried out a…
The deformation behaviour and fracture mechanisms of high-density polyethylene (HDPE), polypropylene (PP) and polyamide 6 (PA 6) are investigated experimentally under different stress states and at different crosshead speeds of 1, 20 and…