The theory of critical distances (TCD) has been applied to predict notch-based fracture and fatigue in a wide range of materials and components. The present paper describes a series of projects in which we applied this approach to human…
Mechanical components fabbricated with quenched and tempered steels, exhibiting mixed microstructures as derived from slant quench conditions, are frequently encountered in the industrial practice, owing to a tendency to employ quite low…
Ultrasonic fatigue tests were carried out on stainless steel AISI 316 and 304, under two modalities: at room temperature and in immersion (water for 316 and antifreeze for 304 steels); all tests were carried out with a loading ratio R=-1.…
Microstructure influence on fatigue crack propagation resistance in five different ductile cast irons (DCI) was investigated. Four ferrite/pearlite volume fractions were considered, performing fatigue crack propagation tests according to…
Europe has a number of ancient riveted metallic bridges, constructed during the second half of the 19th century up to the middle of the 20th century, which are still in operation. In this paper, a unified approach is presented to generate…
Metallic structural components, placed in contact with other bodies while experiencing vibrations in operating conditions, are susceptible to fretting, which can have a significant impact on their fatigue performance. Although extensive…
The exhaustion of constructive ways for increasing the service life of parts has led to the development of new methods which can improve their material properties during operation under various loading conditions. Laser shock peening (LSP)…
Shape memory property characterizes the behavior of many Ti based and Cu based alloys (SMAs). In Cu-Zn-Al SMAs, the original shape recovering is due to a bcc phase that is stable at high temperature. After an appropriate cooling process…
Magnesium (Mg) alloys are attractive as structural materials due to their light weight and high specific strength. It is well known that Mg alloy has hexagonal close-packed (HCP) structure and only basal slip or twinning can operate during…
Austenitic stainless steel (JIS-SUS304L) with a bimodal harmonic structure, which is defined as a coarse-grained structure surrounded by a network of fine grains, was fabricated using powder metallurgy to improve both the strength and…
Ultra-high-strength steels (with tensile strength higher than 980 MPa) are widely used in automobile manufacturing owing to their lightweight that contributes to fuel efficiency. The fatigue strength of ultra-high-strength steels with a…
This study reports an experimental investigation of the fatigue and fracture resistance of R350HT, a heat-treated pearlitic rail steel with refined microstructure used in rails. Monotonic tensile, rotating bending, linear elastic plane…
The work is devoted to the experimental study of heat dissipation process caused by fatigue crack propagation. To investigate a spatial and time temperature evolution at the crack tip set of experiments was carried out using specimens with…
This work is devoted to the comparative analysis of three techniques for measurement of energy dissipation in metals under fatigue crack propagation: original contact heat flux sensor, post-processing of the infrared thermography data and…
Due to their severe operating conditions, many industrial components are subjected to complex combinations of cyclic mechanical stresses and thermal pressures. These combinations are responsible for the initiation and propagation of…
Part-through surface or corner 2D cracks are commonly found in structural components, even because practically all fatigue cracks tend to start this way. It is a reasonable hypothesis to model them assuming the shape of their fronts is…
Blades of combustion turbines are extremely loaded turbojet elements, which transmit operative energy onto a rotor. Experiences of many years indicate, that cracks initiation and propagation in the blades during the operation time can…
This study has used the strain energy density (SED) approach to evaluate the stress intensity factor (SIF) of cracked cruciform welded joints in Hardox 450 steel. A microstructural analysis was made of Hardox 450 steel which is composed of…
Some numerical studies of crack propagation are based on using constitutive models that account for damage evolution in the material. When a critical damage value has been reached in a material point, it is natural to assume that this…
The monitoring of a heat dissipation process can give an important information about kinetics of deformation process and current crack propagation rate. The work is devoted to the theoretical and experimental study of the problem. The…
Two cracks, initiated from the opposite tips of a central notch inclined by 45°, were considered in cruciform specimens made of Ti6246. A static load was applied to a cruciform arm while a cyclic load was applied along the other arm.…
While Additive Manufacturing (AM) of polymers has matured from rapid prototyping to functional production, the layer-wise fabrication process introduces significant mechanical anisotropy and microstructural heterogeneity, which complicates…
In this paper, an experimental procedure to evaluate the elastic-plastic J-integral at the tip of a fatigue crack is presented. According to this new approach, the elastic component of the J-integral is derived from Thermoelastic Stress…
In this work, the effects of natural particles on the micro failure mechanisms and static strength of an epoxy are studied using scanning electron microscope (SEM) technique. To this end, bulk specimens and adhesively bonded single lap…
A three-parameters model for the interpolation of fatigue crack propagation data is proposed. It has been validated by a Literature data set obtained by testing 180 M(T) specimens under three different loading levels. In details, it is…
This study examines the fracture toughness of Al6061 alloy-based hybrid composites reinforced with silicon carbide particles and cenosphere microspheres. Aluminum alloy Al6061 is widely utilized in structural applications due to its…
In this work, the effects of chloride-induced corrosion on tempcore B400c and B450c steel grades are evaluated, in terms of corrosion resistance and mechanical characteristics, after the performance of Tensile and Low Cycle Fatigue…