The work is devoted to the experimental study of heat dissipation process caused by fatigue crack propagation. To investigate a spatial and time temperature evolution at the crack tip set of experiments was carried out using specimens with…
In this research, the variational mode decomposition (VMD) method is used for the drive-by health monitoring of bridges. Firstly, the problem of a half-trailer tractor moving over a bridge is formulated. Next, a Finite Element (FE) code is…
The influence of the austenite (γ) phase fraction on the hydrogen embrittlement of duplex stainless steel is investigated. Heat treatments are performed to create two duplex stainless steel specimens, containing 50% and 44% of austenite…
Ultra-high-strength steels (with tensile strength higher than 980 MPa) are widely used in automobile manufacturing owing to their lightweight that contributes to fuel efficiency. The fatigue strength of ultra-high-strength steels with a…
In the present work, the fracture performance of pre-cracked reinforced concrete beams was investigated numerically and experimentally. Experimental and numerical programs were designed to examine the effect of beam width, b, (120 and 250…
Microstructural characteristics, monotonic and strain-controlled cyclic axial behaviors of AW2099-T83 Aluminum-Lithium alloy were investigated. Grain sizes and structures are not uniform in the different orientations studied. High strength…
The increase in life expectancy and attention to the quality of life of elderly people spurred the need, in the last decades, to increase the capabilities of medical and surgical techniques. Among these, the development of prosthetic…
The stability of the landfill is an environmental issue. The collapse of the landfill causes environmental pollution and influences human life. In the present study, the crack on the cover of the landfill was simulated. Rankine’s theory…
In this paper, an additional criterion was introduced to evaluate the composite repair systems using the limit load analysis. The plastic collapse pressure of API 5L X65 PSL2 steel pressure vessel structure with crack defect is numerically…
Under the cold impact of liquid nitrogen, the shale suffers from the significant freezing damage, which provides the possibility of liquid nitrogen fracturing. Moreover, shale fracturing assisted by liquid nitrogen can effectively reduce…
The present authors have previously proposed a novel ‘plastic inclusion’ approach for dealing with the local plasticity which occurs at the tip of a growing fatigue crack. This meso-scale model provides a modified set of crack tip stress…
Due to the substantial need to continuously ensure safe excavations and sustainable operation of deep engineering structures, structural health monitoring based on remote sensing techniques has become a prominent research topic in this…
Digital image correlation (DIC) is a technique in experimental mechanics to acquire full-field measurement data of displacements and deformations from the surface of specimens or components. Especially for the investigations of cracks it…
The impact behaviour of 6061 alloy with trace amount of 0, 0.04, and 0.08 wt.% Sn was studied in the as-cast (AC), as-roll (AR) and peak-age roll (PAR) processing state. Additionally, the fracture mechanism was also studied in the AC and…
This paper provides the background for practical applications of nonlinear fracture resistance parameters for structural integrity assessment of aviation structures with initial cracks. The subject of this numerical study is a fragment of…
The paper describes the results of an experimental study of a polyurethane material treated by ion implantation technology. The problems of crack growth in the near-surface layer carbonized by ion treatment were investigated using digital…
PMMA has important micro structural heterogeneities such as cavities, and its elastic behavior is greatly affected by the presence of defects that may imply its weakening and cause failure. In areas of high concentrations of stress and due…
Structural failure assessment approaches take into account local parameters, specimen geometry, loading and material. In the case of welded joints, in addition to these parameters, consideration must be given to the effect of the…
In the field of composite materials, extensive research has been undertaken on aluminum-graphite composites. However, a research gap has been identified regarding the specific influence of nano-sized graphite particles on their fracture…
Additive manufacturing techniques continue to develop and cover all industrial fields. However, the performances of aspect and mechanical behavior of the parts obtained by this process remain to be mastered and are still the subject of…
This work constitutes a contribution to the analysis of the behavior of beams reinforced by composite materials. The analysis was made by a study on concrete elements, and in pre-cracked reinforced concrete then reinforced with carbon…
Structures subjected to severe loads, such as earthquakes, often develop cracks at the beam-column joints, underscoring the significance of these regions in design. This study focuses on a comparative analysis of beam-column joints…
Laboratory tests have been conducted to investigate the effects of thermal damage on diorite under microwave irradiation. The sample rocks were heated to high temperature range of 300 to 800 ℃ in a single-mode microwave furnace. The…
This research examines the performance of reinforced lightweight concrete beams subjected to several degrees of damage (50%, 60%, 70%, and 100%). It can use a sheet made of Carbon Fiber Reinforced Polymer (CFRP) to reinforce. The Full…
A new class of material characterized by mechanical properties close to the traditional low and medium carbon steel is the Ductile Cast Irons (DCIs). High castability and low production costs allow them to be used in many fields, ranging…
This paper investigates the combined effect of corrosion and fatigue on the growth of cracks that arise from natural corrosion in steel bridges. It is shown that if these two effects need to be simultaneously analyzed. If not, then the…
Most techniques of measuring the stress intensity factor (SIF) in the cracking process assume a crack in a planar medium. Currently, there is no effective approach for curved brittle shells, particularly for non-developable cases, i.e.…
The paper analyses the fatigue tests of a specimen made of 16Mo3 steel and 6082-T6 aluminium alloy performed under bending and tensile conditions. It has been shown that in the case of bending of the 16Mo3 steel specimen, in low cycle…
Over the last two decades, piezoelectric actuators have emerged as a promising solution for structural repair. In this work, initially the stress intensity factor (SIF) estimation using the finite element (FE) approach at crack tips in…
Different options that rely on fracture mechanics are currently used in engineering during the design and assessment of components. One of the most important aspects is the time taken for a crack to extend to its critical size. If this…
Pipelines are considered as a major tool to transport hydrocarbons due to its important role in transporting fluids taking into account the operating conditions. Despite the importance of the elbow which considered as a critical part in…
This paper aims to disclose the influence law of cracks on instantaneous and long-term deflections of reinforced beam. For this purpose, four concrete beams were created, pre-loaded to varied degrees of cracking, and reinforced with carbon…
Recent developments in the field of replacing and generating human tissues have led to a renewed interest in finding alternative materials or composites that enhance the development of these technologies. Therefore, the main goal of the…
The study presents and compares an application of two procedures to identify the crack tip location in PVC Sent samples under a uniaxial tensile test based on the image processing method. An IDS camera captures several photos of the PVC…
A critical problem in the application of metal matrix composites is the presence of high residual thermal stresses induced during the development process. These thermally induced stresses are generally detrimental to the service life of…
In this study, the finite element method is used to analyze the effect of corrosion and the behavior of inclined cracks of an aluminum plate Al 2024 -T3 under thermomechanical loading. The effects of the inclination of the crack and the…
Slow strain rate stress corrosion test of X80 steel in the natural seawater are carried out to study to effect of dissolved oxygen on the sensitivity of stress corrosion. Scanning electron microscope (SEM) combined electrochemical…
The criteria for optimizing shock-wave modes to increase the fatigue life of aircraft engine alloys are discussed with reference to laser shock peening (LSP). They are based on the self-similarity of plastic wave fronts and the kinetics of…
The flexural behavior of lightweight concrete two-way slabs is investigated in this work, with a focus on the strengthening or repairing method of externally attaching carbon fiber-reinforced polymer (CFRP) sheets. Five 1000 mm by 1000 mm…
Phase-field models have become a powerful tool to simulate crack propagation. They regularize the fracture discontinuity and smooth the transition between the intact and the damaged regions. Based on the thermodynamic function and a…
Cracks in clayey soil cause a reduction in the seismic loading capacity which can lead to structural failures. Seismic acceleration is the primary cause of crack propagation and damage to the earth's structure. This study investigated the…
Mixed mode crack propagation analysis has been more accessible with the development of new numerical tools, allowing to evaluate the influence of non-mode I loadings in the crack path and in the growth rate. The aim of this work is to…
In this work, the effects of natural particles on the micro failure mechanisms and static strength of an epoxy are studied using scanning electron microscope (SEM) technique. To this end, bulk specimens and adhesively bonded single lap…
Dynamic loading on composite components may induce damages such as cracks, delaminations, etc. and development of an early damage detection technique for delaminations is one of the most important aspects in ensuring the integrity and…
This paper attempts to disclose the damage mechanism of reinforced concrete plate-column structure under room temperature and fire. Several tests were carried out to record the law of crack development on the plate surface under room…
This work describes a two-dimensional numerical model that allows detecting the appearance of cracks and calculating their propagation in elements made of laminated bamboo, under tension and shear. This composite material has long parallel…