The crack growth behavior of the aluminum alloy 6061 T651 was investigated using cruciform specimens with a measurement area of 120 x 120 x 2 mm3 with two center crack configurations of the starting notch parallel to one of the loading…
This paper discusses the relationship between the stress response and the microstructure under tension-torsion multiaxial proportional and nonproportional loadings. Firstly, this paper discusses the material dependency of additional…
For multiaxially-loaded parts several stress-based fatigue assessment concepts are applicable mostly taking uniaxial test results as basis. These approaches work well in case of proportional loading states, but on contrary, for…
Several methods can be used to estimate elastoplastic (EP) notchtip stresses and strains from linear elastic calculations, providing EP stress and strain concentration factors. For uniaxial load histories, Neuber’s and Glinka’s rules are…
The influence of the non-proportional loadings on the fatigue life depends on the material ductility. Ductile materials react with a shortening of lifetime compared to proportional loading conditions. For a semiductile material there is…
Many engineering structures are exposed to non-proportional fatigue loading. However, at the critical location of crack initiation, often only one of the load sequences dominates – the individual load cases result in different crack…
In this work, the performance of the SSF criterion is evaluated under variable amplitude loading conditions. The main objective was to inspect the validity of the hypothesis in which the SSF damage map remains valid for any high strength…
The present paper aims to discuss a frequency-domain multiaxial fatigue criterion based on the critical plane approach, suitable for fatigue life estimations in the presence of proportional and non-proportional random loading. The…
This study aims to investigate fatigue damage resulting from multiaxial fatigue, proportional and/or nonproportional, loading by analyzing stresses and strains over a full domain around a representative stress-strain element. Plain…
Materials can be classified as shear or tensile sensitive, depending on the main fatigue microcrack initiation process under multiaxial loadings. The nature of the initiating microcrack can be evaluated from a stress scale factor (SSF)…
Multiaxial fatigue behavior is an important topic in critical structural components. In the present study the biaxial-planar fatigue behavior of a powder metallurgical TRIP steel (Transformation Induced Plasticity) was studied by taking…
Experimental tests were conducted on additive manufactured Ti-6Al-4V titanium alloy to investigate the mechanical and crack properties under multiaxial cyclic loading. Selective Laser Sintering technique (SLS) was employed to fabricate…
This paper presents a simple method of determining stresses and strains and a severity of loading history under non-proportional loadings with defining the rotation angles of the maximum principal stress and strain in a three dimensional…
This paper investigated the static and dynamic behaviors of isotropic cracked simply supported beam using finite element analysis (FEA), ANSYS software. Modal and harmonic vibration analysis of intact and damaged beam were performed in…
The aim of the present research is to check the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating the fatigue strength of friction stir (FS) welded tubular joints of Al 6082-T6 subjected to in-phase and out-of-phase…
The present paper investigates the multiaxial fatigue strength of sharp V-notched components made of titanium grade 5 alloy (Ti-6Al-4V). Axisymmetric notched specimens have been tested under combined tension and torsion fatigue loadings…
This paper focusses on discussing equivalent stress intensity factors and kink angles after a change of mode-mixity from one cycle to the next and when the mode-mixity changes continuously during the fatigue cycles. Thin-walled tubes with…
Welded joints are frequently locations for cracks initiation and propagation that may cause fatigue failure of engineering structures. Biaxial or triaxial stress-strain states are present in the vicinity of welded joints, due to local…
T Multiaxial creep-fatigue tests under non-proportional loading conditions with various strain rates were carried out using a hollow cylinder specimen of a high chromium ferritic steel at 823K in air to discuss the influence of…
Multiaxial fatigue is a challenging problem and, consequently, a number of methods has been developed to aid in design of components and assemblies. Following the complexity of the problem, these approaches are often elaborate and it is…
An experimental campaign was carried out on thin-walled tubes under tension and torsion. The results from experiments are measured and compared. It is observed that cracks follow a shear-dominated growth pattern with increasing crack…
Fatigue life depends strongly on irreversible contributions that accumulate during cyclic loading and unloading of structures. However, the correct identification of the loading path in terms of uniaxial or multi-axial stress states…
The present paper investigates the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating multiaxial fatigue strength of aluminium friction stir (FS) welded joints. Having developed a bespoke joining technology…
Selected methods for calculating notch tip strains and stresses in elastic–plastic isotropic bodies subjected to multiaxial monotonic loading were compared. The methods use sets of equations where hypothetical notch tip elastic strains and…
The aim of this work is to investigate stress gradient effects on the fatigue life estimation of notched Al 7050-T7451 specimens under combined torsion and push-pull loading conditions. Initially, simple push-pull and torsion fatigue tests…
Most of the prior studies on the prediction of fatigue lives have been limited to uniaxial loading cases, whereas real world loading scenarios are often multiaxial, and the prediction of fatigue life based upon uniaxial fatigue properties…
Models proposed to study the multiaxial fatigue damage phenomenon generally lack probabilistic interpretation due to their deterministic form. This implies failure compulsory happening at the plane exhibiting the maximum damage value…
A new fatigue testing device has been developed to test specimens under biaxial loading at 20 kHz. A flat smooth specimen with a disc geometry is placed on a torus frame and cyclically loaded at the center of its upper face. Disc bending…
This study discusses fatigue properties of low carbon steel, type SS400 steel, under non-proportional loading. Multiaxial fatigue tests under proportional and non-proportional loading conditions with various stress amplitudes were carried…
Variational principle of brittle fracture mechanics is employed to predict the crack path in an infinite wedge under a concentrated tensile force. The weight function in basic equation of variational problem is assumed to be proportional…
Vast number of theoretical and experimental works has been devoted to the study of discontinuous plastic deformation (the Portevin-Le Chatelier effect), which manifests itself for most widely used alloys in certain ranges of both…
In this investigation the relationship between J-integral and CTOD is studied considering a Compact Tensile (CT) and Single edge notched bend (SENB) specimens using finite element analysis. The magnitude of CTOD is estimated by…
The work is devoted to experimental study of heat flow evolution at the fatigue crack tip during biaxial loading. The plane samples of titanium alloy Graid-2 with thick of 1 mm were weakened by notch to initiate fatigue crack at the center…
Damage in RC structures causes the degradation of stiffness and frequency parameters. In this study, the relationship between the two coefficients and damage severities is numerically investigated considering a three-dimensional (3D)…
The paper presents the results of tests on the fatigue crack growth for a constant moment amplitude under combined bending with torsion in the aluminium alloy AW-2017A-T4. The tests were performed under different values of the load ratio…
The characterization of ductile damage evolution, and its description, have been the object of extensive research in the continuum damage mechanic field. Many different models have been developed since the pioneering works carried out a…
A series of strain-controlled multiaxial low cycle fatigue (LCF) tests under proportional and non-proportional loading conditions have been conducted on notched specimens. Cylindrical bars of Al 6061 aluminum alloy and AISI 316L stainless…
A lot of trans-femoral amputation patients experience skin breakdown due to the pressures and shear stresses in the stump-prosthesis interface. In this study, a finite element model was employed to investigate the stresses at the stump…
This work is dedicated to the development of a fracture model for an elastic-brittle solid with statistically distributed strength characteristics of subregions and the application of this model to describe fracture processes of bodies…
10.3221/IGF-ESIS.74.05
In fracture mechanics (domain of cracked environments), it is concerned to forecast the behavior of the structures until their ruin. Friction Stir Welding (FSW) is a new process for solid-state joining, it can weld high strength aluminum…
Carbon fiber reinforced plastic (CFRP) materials used for lightweight aircraft structures are susceptible to low velocity accidental impacts during manufacture and while in service. In this study the CFRP laminates subjected to low…
We propose a method of construction of non homogeneous solutions to the problem of traction ofa bar made of an elastic-damaging material whose softening behavior is regularized by a gradient damage model.We show that, for sufficiently long…