Fatigue design is of vital importance to avoid fatigue small crack growth in engineering structures. This study shows that the critical fatigue design stress can be defined below the usual endurance limit, considered in rules and codes.…
In the present paper, mathematical models are proposed in order to analyze the strength of pinloaded lugs with semi-elliptical crack and through-the-thickness crack. The crack growth investigation of considered crack configurations tackles…
It is generally accepted that fatigue crack growth is retarded after an overload, which has been explained either by plasticity-induced crack closure or near-tip residual stress. However, any interpretation of overload effect is…
Aeroengine manufacturers have to demonstrate that critical components such as turbine disks, made of DA Inconel 718, meet the certification requirements in term of fatigue crack growth. In order to be more representative of the in service…
Fatigue surface crack growth and the in-plane and out-of-plane constraint effects are studied through experiments and computations for aluminium alloy D16T. Subjects for studies are cruciform specimens under different biaxial loading and…
The subject for studies is an aluminium cylindrical hollow specimen with external axial and part circumferential semi-elliptical surface crack undergoing fatigue loads. Both the optical microscope measurements and the crack opening…
There is an ever increasing need for accurate understanding of the fatigue crack growth behaviour in major engineering materials and components. With the move towards more complex, probabilistic assessments, the traditional ‘safe’ or…
This study aims to investigate fatigue growth behaviour in AA7075-T651 under non-proportional mixed mode I and II loads. Fatigue tests were performed under cyclic tension and torsion using a thin-walled tubular specimen with a key-hole…
Crack initiation and propagation have been investigated on the polymeric material ABS (Acrylonitrile Butadiene Styrene), under ultrasonic fatigue testing. Three controlled actions were implemented in order to carry out fatigue tests at…
An important topic of the Collaborative Research Centre TRR 30 of the Deutsche Forschungsgemeinschaft (DFG) is the crack growth behaviour in graded materials. In addition, the growth of cracks in the neighbourhood of regions and through…
Crack trajectories under different loading conditions and material microstructural features play animportant role when the conditions of crack initiation and crack growth under fatigue loading have to beevaluated. Unavoidable…
Additive Manufacturing (AM) is a new innovative technique that allows the direct fabrication of complex, individual, delicate and high-strength products, based on their 3D data. Selective Laser Melting (SLM) is one of the AM processes that…
Nowadays, fibre-reinforced composite materials are widely used in many fields, e.g. automotive and aerospace. Natural fibres such as flax and hemp provide good density specific mechanical properties. Additionally, the embodied production…
Symmetric fatigue in two spring steels is investigated in three groups of specimens. One of the groups (Steel EN10270-1SH/ DIN 17223C – C 0.82%, Mn 0.76%, Si 0.26%) has experienced rotating-bending fatigue in air, and the other two groups…
The paper focuses on the effective resistance and the near-threshold growth mechanisms in the ferritic-pearlitic and the pure pearlitic steel. The influence of microstructure on the shear-mode fatigue crack growth is divided here into two…
Fatigue crack growth (FCG) is associated with irreversible and non-linear processes happening at the crack tip. This explains different problems observed in the use of da/dN-?K curves, namely the inability to explain stress ratio and load…
The influence of the joint line remnant (JLR) on tensile and fatigue fracture behaviour has been investigated in a friction stir welded Al-Mg-Sc alloy. JLR is one of the microstructural features formed in friction stir welds depending on…
This article deals with the locally multiaxial fatigue behaviour of high strength steel. To this end, the influence of the cracking path deflections (at the micro level) on the plasticity-induced fatigue crack growth is analyzed. With…
The S-version Finite Element Method (FEM) is known as a global-local superimposed approach that consists of two separate meshes referred to as global and local cracks. The relationship between the energy release rate and the Stress…
An edge crack propagation in a steel bar of circular cross-section undergoing multiaxial fatigue loads is simulated by Finite Element Method (FEM). The variation of crack growth behaviour is studied under axial and combined in phase…
Fatigue crack growth (FCG) rates have traditionally been formulated from fracture mechanics, whereas fatigue crack initiation has been empirically described using stress-life or strain-life methods. More recently, there has been efforts…
The hydrogen effect on the fracture toughness and fatigue crack growth behaviour in the martensitic high strength steel is investigated. The secondary ion mass spectrometry method has been employed to analyse the distribution of hydrogen…
This work presents an in-depth study of the low-cycle fatigue behaviour of ferritic-pearlitic HSLA-420 high-strength steel sheets, with emphasis on the influence of loading direction on fatigue life and damage mechanisms. Plastic…
In this study, a generalized Barenblatt and Botvina dimensional analysis approach to fatigue crack growth is proposed in order to highlight and explain the deviations from the classical power-law equations used to characterize the fatigue…
The present paper addresses experimentally the high temperature fatigue of 40CrMoV13.9 steel and the effect of surface roughness on fatigue strength and crack initiation. The 40CrMoV13.9 steel is widely used in different engineering high…