The non-destructive evaluation of defects by automatic procedures is of great importance for structural components. Thanks to the developments of the non-contact ultrasonic techniques, the automation of the inspections is gaining a…
High resolution synchrotron X-ray tomography has been used to obtain 3D images of arrested cracks initiated at small artificial defects located on the surface of cylindrical steel specimens subjected to mode I fatigue loading. These…
The use of carbon-fiber composite materials (CFRP) in critical cases implies an increase in the resistance to the stability of their mechanical properties. For the purpose of in-depth analysis of defects in the experiments, an integrated…
This study aims at providing a better understanding of the effects of both microstructure and defect on the high cycle fatigue behavior of metallic alloys using finite element simulations of polycrystalline aggregates. It is well known…
The objective of the present paper is to clarify the effect of defect length in depth direction on rolling contact fatigue (RCF) crack propagation in high strength steel. RCF test and synchrotron radiation micro computed tomography (SR…
The modern ideas about of quality of products are based on the principle of the absolute satisfaction of requirements of recommendations of the buyer. A presence of surface defects of steel-smelting and rolling origin is peculiar to the…
The presence of grouting defects emanating from construction operations constitutes a major threat to the structural integrity of the grouted sleeve connection of precast concrete members. This work presents a location-based assessment of…
The aim of this work is a review of scientific results in the literature, related to the application of thermographic techniques to composite materials. Thermography is the analysis of the surface temperature of a body by infrared rays…
Detection and quantitative estimation of deep defects in multi-layered structures is an essential task in a range of technological applications, such as maintaining the integrity of structures, enhancing the safety of aging aircraft, and…
The microstructural origins of premature fatigue failures were investigated on a variety of forged components manufactured from AZ80 and ZK60 magnesium, both at the test specimen level and the full-scale component level. Both stress and…
In rolling contact fatigue (RCF), cracks usually initiate from inclusions beneath the surface and propagate to the contact surface. In the present study, synchrotron radiation computed laminography (SRCL) imaging was performed to observe…
An experimental study was conducted to investigate the influence of operational defects, such as surface scratches and dents, on the residual mechanical properties of glass fiber-reinforced plastic (GFRP) during quasi-static tensile and…
The study focuses on examining the impact of internal manufacturing defects (voids and wrinkles) on the mechanical behavior of structural carbon fiber reinforced polymers (CFRP) under shear loading. Specimens of VKU/VSE1212 material with a…
This paper explores the effect of internal technological defects on the fatigue life of carbon fiber reinforced plastic (CFRP) under simple loading waveforms. One conducted experiments on CFRP specimens with embedded artificial defects…
In this paper, we try to use the finite element method of 2-D axisymmetry to solve problems in eddy current testing problems where the main idea is detecting crack's shape using the NDT-EC. Results are given for a simple eddy current…
The company DRC (pipe repair Department) located within the SONATRACH Company of oil and gas in Algeria, which is responsible for the repair of pipelines for the transport of gas or crude petroleum, will rehabilitate old pipes that have…
The structures of the hydraulic excavator and the crane have numerous one-sided welded joints. However, attachments with box like structures are difficult to weld at both sides. Therefore, high accurate evaluation method is needed. In this…
A need to timely reveal operational damages and technological defects requires a prompt control of states of structures made from composite materials and their consequent repairs aimed at service life extension. This work is devoted to the…
A356-T6 cast aluminum alloy is a light weight structural material, but fatigue crack initiates and propagates from a casting defect leading to final fracture. Thus it is important to eliminate casting defects. In this study, friction stir…
The behavior of short cracks that depart from elastoplastic notch tips is modeled to estimate the stresses required to initiate and to propagate cracks in notched structural components, and to evaluate the size of tolerable crack-like…
The research focuses on examining the impact of technological defects, specifically "dry-spot" and "wrinkles," on the mechanical behavior and buckling resistance of structural composites. The investigation of the buckling phenomenon was…
The structures of the hydraulic excavator and the crane have numerous one-sided welded joints. However, attachments with box like structures are difficult to weld at both sides. Therefore, high accurate evaluation method is needed. In this…
The work is devoted to the experimental and numerical investigation of thermodynamic aspects of the plastic deformation in Armco iron. Dissipation and stored energies was calculated from processed experimental data of the surface…
The present study of Ti6Al4V alloy production via Electron Beam Melting (EBM) represents a cutting-edge research topic impacting different strategic engineering applications. This can be attributed to the widespread use of this alloy and…
Brittle failure of components weakened by cracks or sharp and blunt V-notches is a topic of active and continuous research. It is attractive for all researchers who face the problem of fracture of materials under different loading…
Extra-deep drawing is one of the most important sheet metal forming processes. The appearance of rupture and wrinkling are the most commonly encountered problems in this process. These defects are also very common at a local company…
A simple beam model for the evaluation of tile debonding due to substrate shrinkage is presented. The tile-adhesive-substrate package is modeled as an Euler-Bernoulli beam laying on a two-layer elastic foundation. An effective discrete…
The paper contains plane strain analysis of uniformly stretched plate working in creep condition. The plate contains initial defects in forms of central and/or edge cracks working in mode I. These cracks are modelled by attributing…
The main aim of this study is to assess the effectiveness of a composite repair system in severely corroded circumferential welds in super duplex stainless steel pipes as a preventive measure against the premature corrosion damage at the…
In this work, a micromechanical model is used in order to predict the failure surface of cement concrete subject to multi-axial compression. In the adopted model, the concrete material is schematised as a composite with the following…
Bearings, considered crucial components in rotating machinery, are widely used in the industry. Bearing status monitoring has become an essential step in the deployment of preventive maintenance policy. This work is part of the diagnosis…
The use of Ni-Ti alloys in the practice of endodontic comes from their important properties such as shape memory and superelasticity phenomena, good corrosion resistance and high compatibility with biological tissues. In the last twenty…
A set of heterogeneous and homogeneous materials differing in their brittle and ductile characteristics (granite, marble, silica ceramics, silicon carbide, organic glass) were subjected to impact damaging by a falling weight. Multiple…
This article deals with identifying defects of layered high strength steel materials with the help of tomography measurement. Test samples were made of S960 High Strength Steel to which layers of either aluminium bronze, hardchrome, cobalt…
This article defines the main actions planned in the procedure of non-destructive testing and analysis of defects in the BK1 industrial mill of the cement plant of the GICA group. One of the subjects attracting the attention of researchers…
A fluidic amplifier is a crucial automatic control component in a liquid jet hammer used to drill hard formations in the oil industry. This study aims to determine the true causes of the fracture failure of baseplates in a fluidic…
In the present paper, fatigue tests were performed on sand-blasted AlSi10Mg samples produced by Direct Metal Laser Sintering (DMLS). The effect of sand-blasting on surface properties was evaluated by roughness and residual stresses…
Manufacturing defects are inherent to any manufacturing process. However, in composite materials they might be unavoidable, e.g. ply waviness or even folds of plies are present in complex shaped parts during high pressure resin transfer…
Discrete systems are modeled as a network of nodes (particles, molecules, or atoms) linked by nonlinear springs to simulate the action of van der Waals forces. Such systems are nonlocal if links connecting non-adjacent nodes are…
This paper deals with the fatigue assessment of cast steel defects in terms of macroscopic shrinkage porosity. Within preliminary studies, a generalized Kitagawa diagram GKD was established by numerical analyses of V-notched specimens with…
Defects of concrete piles can occur at any point during the construction of piles. Most common types of pile integrity issues are; presence of voids, inconsistency in concrete mix, entrapped groundwater or slurry, and geometric…
Predicting the failure of carbon fiber composites remains a challenge due to the complex evolution of damage, where the collective behavior of defects like pores and microcracks dictates material strength. The objective of this work is to…
Sensitivity to small defects under torsional fatigue loading condition is examined in the high cycle fatigue regime. Fatigue crack initiation and small crack growth behaviors were observed during fatigue testing and fractographic…
Ductile cast irons (DCIs) are characterized by a wide range of mechanical properties, mainly depending on microstructural factors, as matrix microstructure (characterized by phases volume fraction, grains size and grain distribution)…
This study develops stress intensity factor (SIF) solutions for cladded WWER reactor pressure vessel nozzles subjected to pressurised thermal shock loading. Although finite element analysis is widely used for fracture assessment…
Radiation effects lead to significant reduction in ductility during the life of the components used in nuclear reactors. Sharp change in fracture toughness at lower temperature in Body Centered Cubic (BCC) materials as compared to Face…
Ultra-high performance concrete (UHPC), a kind of composite material characterized by ultra high strength, high toughness and high durability. It has a wide application prospect in engineering practice. But there are some defects in…
The reduced state of stress triaxiality observed in shallow cracked components allows an increased capacity to resist crack propagation compared to that observed in deeply cracked specimens. This may be regarded as a higher fracture…
The three dimensional growth of fatigue cracks in samples of nodular graphite cast iron is characterized using laboratory X-ray computed tomography. The cracks grow from laser machined artificial defects, their development is monitored in…
Additive manufacturing has been recently employed in industrial sectors with the fundamental requirement for zero defect parts. Technological developments in additive manufacturing notwithstanding, there continues to be a scarcity of…