The influence of fiber orientation on the crack propagation behavior was studied with single edgenotched specimens which were cut from an injection-molded plate of short-fiber reinforced plastics of polyphenylenesulphide (PPS) reinforced…
Fretting fatigue experiments aim to represent industrial problems and most of them endure variable loading. Being able to assess lifetime of assemblies, especially for low propagation rate conditions, is essential as experimental…
It is generally accepted that fatigue crack growth is retarded after an overload, which has been explained either by plasticity-induced crack closure or near-tip residual stress. However, any interpretation of overload effect is…
In this paper, crack propagation in Advanced Gas-cooled Reactor (AGR) graphite bricks with ageing properties is studied using the eXtended Finite Element Method (X-FEM). A parametric study for crack propagation, including the influence of…
Crack closure influences fatigue crack growth rate and must be included in the design of components. Plasticity induced crack closure is intimately linked with the crack tip plastic deformation, which becomes residual as the crack…
The paper deals with the Stress Intensity Factor assessment of cracks at the intersection of holes loaded by internal pressure. Triangular flaws are considered at the intersection of two holes inside a specific specimen. The research…
While a long stable crack propagation phase was observed during experiments of complex welded components, very conservative assessments of the fatigue life were achieved in the past. The difference was explained by the stress gradient…
This work is aimed at reproducing numerically a campaign of experimental tests performed for the development of reinforced panels, typically found in aircraft fuselage. The bonded reinforcements can significantly reduce the rate of fatigue…
Crack propagation simulation began with the development of the finite element method; the analyses were conducted to obtain a basic understanding of the crack growth. Today structural and materials engineers develop structures and…
This paper is devoted to the analysis of the load path effect on I+II+III mixed mode fatigue crack propagation in a 316L stainless steel. Experiments were conducted in mode I+II and in mode I+II+III. The same maximum, minimum and mean…
Brittle fracture in carbon steel has a serious impact on the safety of steel structures. Thus, technology that arrests crack propagation is the final line of protection for such structures. It is such an important issue that conditions…
Crack initiation and propagation have been investigated on the polymeric material ABS (Acrylonitrile Butadiene Styrene), under ultrasonic fatigue testing. Three controlled actions were implemented in order to carry out fatigue tests at…
There is an ever increasing need for accurate understanding of the fatigue crack growth behaviour in major engineering materials and components. With the move towards more complex, probabilistic assessments, the traditional ‘safe’ or…
This paper deals with the fatigue crack propagation behavior of rolled AZ31B magnesium alloy (grain size: approximately 40 ?m). Fatigue crack propagation tests were performed on single edge notched tension specimens at a stress ratio of R…
The fatigue behaviour of concrete has become more important for the design of constructions due to the desire to build slimmer structures, which are more sensitive to fatigue loading. This article aims to evaluate and compare the fatigue…
In this work, the effect of superimposing of isothermal low cycle fatigue loading to the thermomechanical fatigue loading on the crack propagation behavior of the naturally initiated short crack in Low-carbon nitrogen-controlled 316…
The work is devoted to experimental investigation of the laser shock peening (LSP) effect on fatigue crack propagation rate and heat dissipation at the crack tip in specimens made of titanium alloy Grade 2 with a stress concentrator. It is…
This study discusses an effect of additive elements on crack propagation behaviour for low-Ag contain Sn1.0Ag0.7Cu lead-free solders at high temperature. A cyclic push-pull loading tests for four kinds of Sn1.0Ag0.7Cu solders were…
This work aims to study the crack propagation in 12%Cr steel for turbine disks. Creep Crack Growth (CCG) tests on CT specimens have been performed to define the proper fracture mechanics which describes the initiation of the crack…
The goal of the authors’ investigations was determination of the fatigue crack growth in fragments of steel structures (of the puddled steel) and its cyclic behavior. Tested steel elements coming from the turn of the 19th and 20th were…
The paper analyses previously reported work, which uses digital image correlation to measure fatigue crack closure. As well as determining crack opening loads, the information on crack shape may be used to estimate the stress intensity…
In this paper the fatigue crack growth tests were carried out on surface-crack tension (SCT) specimens, made of 7050 and Ti6Al4V alloys, with initial semi-elliptical surface cracks. Pure Mode I conditions were realized on SCT specimens…
This work is devoted to the development of an experimental method for studying the energy balance during cyclic deformation and fracture. The studies were conducted on 304 stainless steel AISE and titanium alloy OT4-0 samples. The…
Fatigue crack initiation and propagation involve plastic strains that require some work to be done on the material. Most of this irreversible energy is dissipated as heat and consequently the material temperature increases. The heat being…
This paper presents new analytical model of asymmetric mixed-mode bending (MMB) specimen of adhesively bonded pultruded GFRP joints. An easily applicable relationship for the calculation of the strain energy release rate of the asymmetric…
Plastics belong to the most complex and probably least understood engineering materials of today. Combining the best aspects of design, mechanical properties and manufacturing, the structural integrity of plastics is on par with aluminium…
The direct identification of the cohesive law in pure mode I of Pinus pinaster is addressed. The approach couples the double cantilever beam (DCB) test with digital image correlation (DIC). Wooden beam specimens loaded in the…
This article deals with the locally multiaxial fatigue behaviour of high strength steel. To this end, the influence of the cracking path deflections (at the micro level) on the plasticity-induced fatigue crack growth is analyzed. With…
In this paper are presented the crack initiation angles obtained in polyurethane (PUR) foams under mixed mode loading. Closed cell rigid PUR foams having three different densities 100, 145, and 300 kg/m3 were investigated. Experiments were…
An analytical model is developed to predict fatigue crack propagation rate under mode I loading in 2024 aluminum alloy with FSW HAZ material characteristics. Simulation of the HAZ local properties in parent 2024 AA was performed with…
Fatigue crack growth (FCG) is linked to irreversible and non-linear processes happening at the crack tip, which explains different problems observed in the use of da/dN-DK curves. The replacement of DK by non-linear crack tip parameters…
For industrial in-series castings, the presence of casting defects, like porosity, geometrically complex intermetallic precipitates and the occurrence of eutectic silicon of varying morphologies, is well known but hard to prevent due to…
The present paper describes a novel experimental technique recently presented that allows one to study interactions between the crack and microstructural barriers with an unprecedented level of ease and detail. The method consists in…
In this study, a numerical strategy for predictive modelling of creep in tension tests for the rectangular plate with a single crack and CT-specimen based on the extended finite element method (XFEM) will be described in detail. A model of…
The aim of this work is the study of the fatigue behaviour of API X60 steel and the influence of thermal and mechanical treatments. The evaluation of the integrity and safety of welded structures dictates the approach taken in this…
Metallic materials dissipate thermal energy when subjected to fatigue. Some of them, due a favorable combination of thermo-physical material properties, exhibit a significant temperature rise, which can be easily measured in-situ by means…
The work is devoted to experimental study of heat flow evolution at the fatigue crack tip during biaxial loading. The plane samples of titanium alloy Graid-2 with thick of 1 mm were weakened by notch to initiate fatigue crack at the center…
Experimental and numerical studies investigating fatigue crack growth were conducted on flat samples made of stainless steel AISE 304 and titanium alloy Grade 2. The heat flux from the crack tip caused by plastic deformation localization…
Mechanical components fabbricated with quenched and tempered steels, exhibiting mixed microstructures as derived from slant quench conditions, are frequently encountered in the industrial practice, owing to a tendency to employ quite low…
Structural failure assessment approaches take into account local parameters, specimen geometry, loading and material. In the case of welded joints, in addition to these parameters, consideration must be given to the effect of the…
Mixed mode crack propagation analysis has been more accessible with the development of new numerical tools, allowing to evaluate the influence of non-mode I loadings in the crack path and in the growth rate. The aim of this work is to…
An analysis to show the capability of moving mesh strategy to predict dynamic crack growth phenomena in 2D continuum media is proposed. The numerical method is implemented in the framework of the finite element method, which is coupled…
The structures in service are subjected to loads whose amplitude varies most often over time. These differences in loading cycle levels will have a direct impact on the propagation of cracks that can lead to accelerations or slowdowns in…
The monitoring of a heat dissipation process can give an important information about kinetics of deformation process and current crack propagation rate. The work is devoted to the theoretical and experimental study of the problem. The…
This paper presents a study on the tensile, fracture, damage, and reliability properties of 3D printed polylactic acid (PLA), based on a series of experiments. The study focuses on polylactic acid (PLA) samples produced using fused…
This work is devoted to the comparative analysis of three techniques for measurement of energy dissipation in metals under fatigue crack propagation: original contact heat flux sensor, post-processing of the infrared thermography data and…
Due to their severe operating conditions, many industrial components are subjected to complex combinations of cyclic mechanical stresses and thermal pressures. These combinations are responsible for the initiation and propagation of…
In the present work, the fracture resistance of a carbon fiber composite under mode I and mode II loading have been experimentally determined. For the mode I and II, the energy release rate G has been determinate for each material. In some…
This study reports an experimental investigation of the fatigue and fracture resistance of R350HT, a heat-treated pearlitic rail steel with refined microstructure used in rails. Monotonic tensile, rotating bending, linear elastic plane…