0000-0003-0273-7746
Abstract
This study examines the changes in microstructure and mechanical properties of friction stir-welded (FSW) dissimilar joints between AA2014-T6 and AA5052-H32 aluminium alloys, with an emphasis on optimizing tool rotation speed for enhanced joint quality. FSW is performed at three different tool rotation speeds (860, 1160, and 1460 rpm) while maintaining a constant welding speed and tool tilt angle of 40 mm/min and 1°, respectively. The joint created at an optimal rotation speed of 860 rpm exhibits outstanding mechanical properties, with an ultimate tensile strength (UTS) of 211 ± 1.0 MPa, a yield strength of 181 ± 1.5 MPa, and an elongation of 16.1%. The joint efficiency, in comparison to the aluminium alloy AA5052-H32, is 93.8%, indicating minimal strength loss relative to the parent material. Vickers hardness tests across the weld cross-section reveal a maximum hardness of 156 ± 1.5 HV in the stir zone, closely matching the hardness of the stronger AA2014-T6 base metal. Fractographic analysis of the FSW joint made at 860 rpm indicates a predominantly ductile failure mode with micro-dimple fracture surfaces, whereas higher tool rotation speeds exhibit brittle characteristics with circular voids and tear ridges.
Keywords
Article history
- ReceivedUntil the next stage: 21 days
- Revision requestedUntil the next stage: 31 days
- RevisedUntil the next stage: 3 days
- AcceptedUntil the next stage: 11 days
- Published
Statements
Funding
About the authors
Mervin A. Herbert
Associate Professor
Mechanical Engineering
Arun Kumar Shettigar
Assistant Professor
Mechanical Engineering
Manjunath Vatnalmath
Assistant Professor
Mechanical Engineering
How to cite
APA
IEEE
MLA
Chicago
Harvard
Vancouver
BibTeX
RIS
Licence
May be shared and adapted, provided appropriate credit is given. Copyright © 2025 N. N. Sathya; Mervin A. Herbert, Arun Kumar Shettigar, Manjunath Vatnalmath.
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Fracture and Structural Integrity (F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit, providing a link to the license, and indicating if changes were made.
Similar articles
Most read articles by the same author(s)
- Manjunath Vatnalmath, V. Auradi, Bharath V Bharath, Anirudh Bharadwaj, Chetan Gowda, Madeva Nagaral, Microstructure, Mechanical and Fractographic behaviour of the Diffusion Welded Joints of AA2219 and Ti-6Al-4V for aerospace applications , Fracture and Structural Integrity: Vol 19 No 71 (2025): January 2025
- R. Sampath Kumar, H. C. Chittappa, Praveena Bindiganavile Anand, Manjunath Vatnalmath, Madeva Nagaral, Effect of B₄C variation on the mechanical, fractographic and tribological performance of hybrid composites Al7075/Gr/ZrO₂ , Fracture and Structural Integrity: Vol 20 No 76 (2026): April 2026
- Annapoorna Krishnappa, Shobha Ramesh, Rajanna Siddagangappa, Srimadhu Ashokkumar, Manjunath Vatnalmath , Virupaxi Auradi, Madeva Nagaral, Influence of hybrid nano Al2O3–ZrO2 reinforcements on microstructure, fracture toughness and fractographic behaviour of Al6061 alloy , Fracture and Structural Integrity: Vol 20 No 76 (2026): April 2026
- C N Vikas, N. Nagesha, Manjunath Vatnalmath, Mr SathyaNarayana N, Microstructure, tensile and fractographic behavior of friction stir welded joints AA6061 and AA2024 , Fracture and Structural Integrity: Vol 20 No 77 (2026): July 2026