In recent years, very-high-cycle fatigue (VHCF) behavior of metallic materials has become a major point of interest for researchers and industries. The needs of specific industrial fields (aerospace, mechanical and energy industry) for…
Crack initiation characteristics and fatigue property of a high-strength steel in very-high-cycle fatigue (VHCF) regime under different stress ratios were investigated in this paper. Fatigue tests were performed at stress ratios of -1…
A large number of mechanical components are subjected to fatigue loading beyond 106 cycles. The VHCF behaviour of smooth specimens has been extensively investigated in the recent years, even if more efforts are necessary to reveal the…
The influence of environmental medias on crack propagation of a structural steel at high and very high-cycle fatigue (VHCF) regimes is investigated based on the fatigue tests performed in air, water and 3.5% NaCl aqueous solution. Crack…
We propose the interpretation of the Finite Fracture Mechanics based on the criticality of damage-failure transition due to specific metastability of free energy release. Multiscale mechanisms of fatigue damage-failure transitions in…
The very high cycle region of the S-N fatigue curve has been the subject of intensive research on the last years, with special focus on axial, bending, torsional and fretting fatigue tests. Very high cycle fatigue can be achieved using…
A new fatigue testing device has been developed to test specimens under biaxial loading at 20 kHz. A flat smooth specimen with a disc geometry is placed on a torus frame and cyclically loaded at the center of its upper face. Disc bending…
The work is devoted to the study of the damage accumulation in iron under gigacyclic fatigue (VHCF) regime. The study of the mechanical properties of the samples with different state of life time existing was carried out on the base of the…
The profile samples prepared by focused ion beam (FIB) in crack initiation region (CIR) and fish-eye (FiE) region of failed specimens subjected to rotary bending (RB) and ultrasonic axial (UL) fatigue testing with various stress ratios (R)…
A new formulation of a Logistic deterministic S-N curve is applied to fatigue data of metallic materials from ancient Portuguese riveted steel bridges. This formulation is based on a modified logistic relation that uses three parameters to…
For industrial in-series castings, the presence of casting defects, like porosity, geometrically complex intermetallic precipitates and the occurrence of eutectic silicon of varying morphologies, is well known but hard to prevent due to…
The criteria for optimizing shock-wave modes to increase the fatigue life of aircraft engine alloys are discussed with reference to laser shock peening (LSP). They are based on the self-similarity of plastic wave fronts and the kinetics of…