The current energy policy envisages extended lifetime for the current nuclear power plants (GEN II NPP). This policy imposes a large research effort to understand the ageing of power plant components. In this goal, it is necessary to…
The behavior of short cracks that depart from elastoplastic notch tips is modeled to estimate the stresses required to initiate and to propagate cracks in notched structural components, and to evaluate the size of tolerable crack-like…
The present paper describes a novel experimental technique recently presented that allows one to study interactions between the crack and microstructural barriers with an unprecedented level of ease and detail. The method consists in…
Fatigue design is of vital importance to avoid fatigue small crack growth in engineering structures. This study shows that the critical fatigue design stress can be defined below the usual endurance limit, considered in rules and codes.…
The present contribution reviews a recently proposed method to rapidly estimate the averaged SED at the tip of short as well as long cracks under in-plane I+II and long cracks under out-of-plane I+III mixed mode loadings. Short cracks are…
The paper presents an experimental analysis of tracking the path of the cracks and crack growth in strengthened or repair reinforced concrete short corbels bonded by carbon fiber fabrics under static and dynamic loads. The reinforced short…
Notches and cracks are usually approximately modeled as two-dimensional problems using solutions from plane elasticity to quantify localized stress/strain concentration effects around their tips. However, they may be associated with high…
This paper deals with the fatigue crack propagation behavior of rolled AZ31B magnesium alloy (grain size: approximately 40 ?m). Fatigue crack propagation tests were performed on single edge notched tension specimens at a stress ratio of R…
In this paper a methodology for evaluating crack initiation under biaxial conditions is presented. The methodology consists of evaluating the crack length automatically with digital processing of highmagnification images of the crack. The…
Crack trajectories under different loading conditions and material microstructural features play animportant role when the conditions of crack initiation and crack growth under fatigue loading have to beevaluated. Unavoidable…
Elastic fracture mechanics commonly defines the fracture resistance of brittle materials within an idealised picture of planar and traction free cracks. An efficient approach to describe the interface conditions in real cracks, such as…
In this work, the effect of superimposing of isothermal low cycle fatigue loading to the thermomechanical fatigue loading on the crack propagation behavior of the naturally initiated short crack in Low-carbon nitrogen-controlled 316…
This is the third part of a short series of paper, revisiting some classical concepts of Linear Elastic Fracture Mechanics. Based on the solution for the single edge notched strip, discussed in Part-II, the present study deals with the…
Semi–empirical notch sensitivity factors q have been widely used to properly account for notch effects in fatigue design for a long time. However, the intrinsically empirical nature of this old concept can be avoided by modeling it using…
This paper presents results of experimental examinations of stress concentration influence to fatigue life of butt welded joints with K-groove, produced from the most frequently used structural steel S355J2+N. One group of experiments…
Symmetric fatigue in two spring steels is investigated in three groups of specimens. One of the groups (Steel EN10270-1SH/ DIN 17223C – C 0.82%, Mn 0.76%, Si 0.26%) has experienced rotating-bending fatigue in air, and the other two groups…
Symmetric fatigue in two spring steels is investigated in three groups of specimens. One of the groups (Steel EN10270-1SH/ DIN 17223C – C 0.82%, Mn 0.76%, Si 0.26%) has experienced rotating-bending fatigue in air, and the other two groups…
This is the first part of a short three-paper series, aiming to revisit some classical concepts of Linear Elastic Fracture Mechanics. The motive of this first paper is to highlight some controversial issues, related to the unnatural…
The analysis of fracture processes which led to shear failure in reinforced concrete beams without transverse reinforcement was performed on the basis of test results from the author’s own experimental investigation and numerical…
The compliance method was first applied to short rod specimens to determine the nonlinear fracture toughness of rock materials by ISRM (International Society for Rock Mechanics) in the 1980s. In this study, utilizing the techniques of the…