Nel presente articolo viene proposta una nuova metodologia di progettazione a fatica, basata sull’utilizzo del metodo delle Curve di Wöhler Modificate, per la previsione della vita a fatica di giunzioni saldate, sia in acciaio che in…
The scatter degree of the fatigue samples is reduced when the nodal force based structural method is used for steel welded joints, while it is still high for aluminum alloy welded joints. Statistical method and rough set theory is used to…
Additive layer manufacturing has recently gained a lot of interest due to the feasibility of producing metallic components directly from a computer-aided design file of the part. Selective laser melting, one of the main additive layer…
In engineering applications, fatigue phenomenon is a key issue and needs to be analyzed in the beginning of design phase in case of any component exposed to alternating loading on operation otherwise catastrophic fatigue failure may cause.…
S-N curve fatigue samples of titanium alloy welded joints have such a comparatively significant scatter, that results in the issue that the fatigue life prediction accuracy is not optimal. In this work, the titanium alloy welded joints'…
A new formulation of a Logistic deterministic S-N curve is applied to fatigue data of metallic materials from ancient Portuguese riveted steel bridges. This formulation is based on a modified logistic relation that uses three parameters to…
The aim of the present paper is to systematically investigate the accuracy of the so-called Modified Wöhler Curve Method (MWCM) in estimating high-cycle fatigue strength of plain and notched engineering materials damaged by in-service…
This paper aims to disclose the damage evolution law of the surface field of argillaceous dolomite. For this purpose, the 3D digital image correlation was combined with the Brazilian test into a new analysis method for the surface field…
In the present paper, the multiaxial fatigue life assessment of notched structural components is performed by employing a strain-based multiaxial fatigue criterion. Such a criterion, depending on the critical plane concept, is extended by…
Partendo dalla osservazione che provini precedentemente danneggiati hanno un limite di fatica differente (vedi Miner) viene esaminato il comportamento di un acciaio soggetto a serie di carichi affaticanti al fine di verificare la…
There has been a trend recently to use specimen geometries for toughness measurement that are more representative of actual flaw geometries in service. A prominent example is the use of single-edge-notched tension specimens for assessment…
Engineering components often contain notches, keyways or other stress concentration features. These features raise the stress state in the vicinity of their apex which can lead to unexpected failure of the component. The Theory of Critical…
Brittleness plays an important role in the brittle failure process of rocks, and is also one of the important mechanical properties of rocks and a key indicator in rock engineering such as hydraulic fracturing, tunnelling machine borehole…
A new critical plane approach based on the modified Manson-Coffin curve method (MMCCM) is presented in this paper for predicting fatigue lifetime under variable amplitude (VA) multiaxial fatigue loading. The critical plane is assumed to…
In this work, a micromechanical model is used in order to predict the failure surface of cement concrete subject to multi-axial compression. In the adopted model, the concrete material is schematised as a composite with the following…
SS 316Ti is widely used in bellows industry and is a good candidate material for high temperature bellows in sodium cooled fast reactor (SFR) systems. Typical operating temperature experienced by SFR systems is around 823K. Design of…
The aim of the present research is to check the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating the fatigue strength of friction stir (FS) welded tubular joints of Al 6082-T6 subjected to in-phase and out-of-phase…
During biventricular pacemaker implantation stents can be applied for coronary sinus lead stabilization to prevent lead dislocations. A lot of issues have been raised in connection with the use of the stent. In some cases the implanted…
This work presents a methodology for life estimation of mechanical couplings subjected to fretting fatigue. In this approach, a stress-based multiaxial fatigue parameter is evaluated at a critical distance below the contact surface. The…
The peculiar geometrical shape and working conditions of crankshafts make fatigue becoming responsible for most of the failure cases in such components. Therefore, improvement of crankshaft performance requires enhancing its fatigue life.…
Marine structures are particularly prone to action of waves, winds and currents with stochastically varying composition, intensities and directions. Therefore, resultant stresses may cause multiaxial fatigue in specific welded structural…
Selected methods for calculating notch tip strains and stresses in elastic–plastic isotropic bodies subjected to multiaxial monotonic loading were compared. The methods use sets of equations where hypothetical notch tip elastic strains and…
The knowlegde of dynamic mechanical properties is useful in all cases where the strain rate sensitivity of metallic materials is an issue, and whenever the actual loading conditions for a structure (either in normal operation or under…
Since the last two centuries, concrete has become the number one building material in the world. Therefore, we are interested in studying the mechanical behavior at failure of this material and calculate its toughness. In this paper, we…
Early damage detection plays an essential role in the safe and satisfactory maintenance of structures. This work investigates techniques use only damaged structure responses. A Timoshenko beam was modeled in finite element method, and an…
Fatigue surface crack growth is studied through experiments and computations for aluminum alloys D16T and B95AT (analogue of 2024 and 7075 aluminum). Subjects for studies are cylindrical hollow specimens with external semi-elliptical…
Due to its physical complexity, fatigue phenomenon inherently presents a significant number of uncertain parameters to be predicted. In uncertainty quantification (UQ), research has demonstrated that even a small variation in uncertain…
Multiaxial high cycle fatigue is a topic that concerns nearly all industrial domains. In recent years, a great deal of recommendations how to address problems with multiaxial fatigue life time estimation have been made and a huge progress…
In order to study the mechanical behavior of reactive powder concrete (RPC) filled square steel tubular columns, this paper designs an eccentric compression experiment for 12 specimens of RPC filled square steel tubular column and studies…
This study concerns the multiaxial static and fatigue strength properties. Short-glass-fibre-reinforced phenolic-resin composites (SGP) molded by injection and compression processes were subjected to tensiontorsion combined static and…
The stepped isostress method (SSM) is an advanced technique which allows the prediction of the long-term behavior and enables the construction of creep master curves of materials with short-term experimental tests. However, the performance…
Fatigue design of welded structures is primarily based on a nominal stress; hot spot stress methods or local approaches each having several limitations when coupled with finite element modeling. An alternative recent structural stress…
The very high cycle region of the S-N fatigue curve has been the subject of intensive research on the last years, with special focus on axial, bending, torsional and fretting fatigue tests. Very high cycle fatigue can be achieved using…
This work analyses the results of a simple forming process of an AA6060 aluminium alloy sheet in order to validate the development of a simulation model based on the finite element method (FEM). This work represents the starting point of a…
This work aims at studying the creep behaviour of 15-15Ti(Si) austenitic steel, under uniaxial stress (range of 300-560 MPa), and its interaction with liquid lead. The steel was tested to verify its sensitivity to Liquid Metal…
The present report presents a fatigue life prediction method for large roller bearings applied in the turret turn table for large loading buoy units. The contact points between wheel and rail in these bearings are subjected to a…
Artificial ground freezing (AGF) is a common technology of shaft sinking through water-bearing strata. The AGF technique is used to create a frozen wall preventing shaft flooding. An additional factor that makes shaft sinking more…
Notches and cracks are usually approximately modeled as two-dimensional problems using solutions from plane elasticity to quantify localized stress/strain concentration effects around their tips. However, they may be associated with high…
The fatigue behaviour of concrete has become more important for the design of constructions due to the desire to build slimmer structures, which are more sensitive to fatigue loading. This article aims to evaluate and compare the fatigue…
Il lavoro verifica l’applicabilità di un modello semplificato agli elementi finiti per l’analisi a collasso post elastico di strutture incollate complesse in parete sottile. Al fine di superare le limitazioni dei modelli di letteratura…
An experimental campaign was developed to study fatigue crack growth in Haynes 230, a Ni-based superalloy. The effects of crack closure were investigated with digital image correlation, by applying two different approaches. Initially, full…
Fatigue cracking of longerons manufactured from Al-alloy AVT-1 for helicopter in-service rotorblades was considered and crack growth period and equivalent of tensile stress for different blade sections were estimated. Complicated case of…
Damage in RC structures causes the degradation of stiffness and frequency parameters. In this study, the relationship between the two coefficients and damage severities is numerically investigated considering a three-dimensional (3D)…
The paper is devoted to theoretical and experimental investigation of materials behavior on postcritical deformation stage (strain softening). Tests results, which confirm theoretical justification of specimen configuration impact on the…
The present paper is concerned with the formulation of an elasto-plastic strain based approach suitable for assessing fatigue strength of notched components subjected to in-service variable amplitude cyclic loading. The hypothesis is…
Selecting the correct objective function is the critical precondition for a successful optimization task. The validity of this condition is also required when optimization algorithms are needed for the inverse identification of the unknown…
Le problematiche relative all’utilizzo delle normative nell’ambito della progettazione a fatica di strutture in leghe di alluminio sono state di recente affrontate in numerosi lavori che hanno messo in luce sia le difficoltà legate al…
This paper presents results of experimental examinations of stress concentration influence to fatigue life of butt welded joints with K-groove, produced from the most frequently used structural steel S355J2+N. One group of experiments…
As often done in design practice, the Wöhler curve of a specimen, in the absence of more direct information, can be crudely retrieved by interpolating with a power-law curve between static strength at a given conventional low number of…
In this paper, a machine learning-based framework is developed to quickly evaluate the structural safety of trusses. Three numerical examples of a 10-bar truss, a 25-bar truss, and a 47-bar truss are used to illustrate the proposed…