Multiaxial fatigue behavior is an important topic in critical structural components. In the present study the biaxial-planar fatigue behavior of a powder metallurgical TRIP steel (Transformation Induced Plasticity) was studied by taking…
The influence of the non-proportional loadings on the fatigue life depends on the material ductility. Ductile materials react with a shortening of lifetime compared to proportional loading conditions. For a semiductile material there is…
Most of the prior studies on the prediction of fatigue lives have been limited to uniaxial loading cases, whereas real world loading scenarios are often multiaxial, and the prediction of fatigue life based upon uniaxial fatigue properties…
For multiaxially-loaded parts several stress-based fatigue assessment concepts are applicable mostly taking uniaxial test results as basis. These approaches work well in case of proportional loading states, but on contrary, for…
Welded joints are frequently locations for cracks initiation and propagation that may cause fatigue failure of engineering structures. Biaxial or triaxial stress-strain states are present in the vicinity of welded joints, due to local…
Materials can be classified as shear or tensile sensitive, depending on the main fatigue microcrack initiation process under multiaxial loadings. The nature of the initiating microcrack can be evaluated from a stress scale factor (SSF)…
This study aims to investigate fatigue damage resulting from multiaxial fatigue, proportional and/or nonproportional, loading by analyzing stresses and strains over a full domain around a representative stress-strain element. Plain…
The aim of the present research is to check the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating the fatigue strength of friction stir (FS) welded tubular joints of Al 6082-T6 subjected to in-phase and out-of-phase…
This paper discusses the relationship between the stress response and the microstructure under tension-torsion multiaxial proportional and nonproportional loadings. Firstly, this paper discusses the material dependency of additional…
Fatigue life depends strongly on irreversible contributions that accumulate during cyclic loading and unloading of structures. However, the correct identification of the loading path in terms of uniaxial or multi-axial stress states…
The aim of this work is to investigate stress gradient effects on the fatigue life estimation of notched Al 7050-T7451 specimens under combined torsion and push-pull loading conditions. Initially, simple push-pull and torsion fatigue tests…
The present paper aims to discuss a frequency-domain multiaxial fatigue criterion based on the critical plane approach, suitable for fatigue life estimations in the presence of proportional and non-proportional random loading. The…
A new fatigue testing device has been developed to test specimens under biaxial loading at 20 kHz. A flat smooth specimen with a disc geometry is placed on a torus frame and cyclically loaded at the center of its upper face. Disc bending…
Many engineering structures are exposed to non-proportional fatigue loading. However, at the critical location of crack initiation, often only one of the load sequences dominates – the individual load cases result in different crack…
This study discusses fatigue properties of low carbon steel, type SS400 steel, under non-proportional loading. Multiaxial fatigue tests under proportional and non-proportional loading conditions with various stress amplitudes were carried…
The present paper investigates the multiaxial fatigue strength of sharp V-notched components made of titanium grade 5 alloy (Ti-6Al-4V). Axisymmetric notched specimens have been tested under combined tension and torsion fatigue loadings…
This paper focusses on discussing equivalent stress intensity factors and kink angles after a change of mode-mixity from one cycle to the next and when the mode-mixity changes continuously during the fatigue cycles. Thin-walled tubes with…
Multiaxial fatigue is a challenging problem and, consequently, a number of methods has been developed to aid in design of components and assemblies. Following the complexity of the problem, these approaches are often elaborate and it is…
The present paper investigates the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating multiaxial fatigue strength of aluminium friction stir (FS) welded joints. Having developed a bespoke joining technology…
In this work, the performance of the SSF criterion is evaluated under variable amplitude loading conditions. The main objective was to inspect the validity of the hypothesis in which the SSF damage map remains valid for any high strength…
Several methods can be used to estimate elastoplastic (EP) notchtip stresses and strains from linear elastic calculations, providing EP stress and strain concentration factors. For uniaxial load histories, Neuber’s and Glinka’s rules are…
Experimental tests were conducted on additive manufactured Ti-6Al-4V titanium alloy to investigate the mechanical and crack properties under multiaxial cyclic loading. Selective Laser Sintering technique (SLS) was employed to fabricate…
Carbon fiber reinforced plastic (CFRP) materials used for lightweight aircraft structures are susceptible to low velocity accidental impacts during manufacture and while in service. In this study the CFRP laminates subjected to low…
The paper presents the results of tests on the fatigue crack growth for a constant moment amplitude under combined bending with torsion in the aluminium alloy AW-2017A-T4. The tests were performed under different values of the load ratio…
A series of strain-controlled multiaxial low cycle fatigue (LCF) tests under proportional and non-proportional loading conditions have been conducted on notched specimens. Cylindrical bars of Al 6061 aluminum alloy and AISI 316L stainless…
Models proposed to study the multiaxial fatigue damage phenomenon generally lack probabilistic interpretation due to their deterministic form. This implies failure compulsory happening at the plane exhibiting the maximum damage value…
This paper presents a simple method of determining stresses and strains and a severity of loading history under non-proportional loadings with defining the rotation angles of the maximum principal stress and strain in a three dimensional…
The work is devoted to experimental study of heat flow evolution at the fatigue crack tip during biaxial loading. The plane samples of titanium alloy Graid-2 with thick of 1 mm were weakened by notch to initiate fatigue crack at the center…
An experimental campaign was carried out on thin-walled tubes under tension and torsion. The results from experiments are measured and compared. It is observed that cracks follow a shear-dominated growth pattern with increasing crack…