This study aims at providing a better understanding of the effects of both microstructure and defect on the high cycle fatigue behavior of metallic alloys using finite element simulations of polycrystalline aggregates. It is well known…
Cracking direction in multiaxial low cycle fatigue is an important research subject because crack initiation and propagation behavior is a physical background for developing an estimation method of multiaxial low cycle fatigue lives.…
Under the typical partial slip conditions under which fretting fatigue takes place, the amount of superficial damage is small. Therefore, the substantial reduction in fatigue life caused by fretting, when compared to plain fatigue, may…
The very high cycle region of the S-N fatigue curve has been the subject of intensive research on the last years, with special focus on axial, bending, torsional and fretting fatigue tests. Very high cycle fatigue can be achieved using…
The present report presents a fatigue life prediction method for large roller bearings applied in the turret turn table for large loading buoy units. The contact points between wheel and rail in these bearings are subjected to a…
Nowadays, many components and structures are subjected to fatigue loading with a number of cycles higher than 107. In this scientific work, the behaviour of two kinds of tool steel was investigated in very high cycle fatigue regime. The…
Sensitivity to small defects under torsional fatigue loading condition is examined in the high cycle fatigue regime. Fatigue crack initiation and small crack growth behaviors were observed during fatigue testing and fractographic…
Fatigue (high- and gigacycle) crack initiation and its propagation in titanium alloys with coarse and fine grain structure are studied by fractography analysis of fracture surface. Fractured specimens were analyzed by interferometer…
Multiaxial high cycle fatigue is a topic that concerns nearly all industrial domains. In recent years, a great deal of recommendations how to address problems with multiaxial fatigue life time estimation have been made and a huge progress…
This paper discusses the relationship between the stress response and the microstructure under tension-torsion multiaxial proportional and nonproportional loadings. Firstly, this paper discusses the material dependency of additional…
Engine components are usually subject to complex loading patterns such as mixed-mode Low Cycle Fatigue Loading due to maneuvering. In practice, this LCF Loading has to be superimposed by High Cyclic Fatigue Loading caused by vibrations.…
A large number of mechanical components are subjected to fatigue loading beyond 106 cycles. The VHCF behaviour of smooth specimens has been extensively investigated in the recent years, even if more efforts are necessary to reveal the…
The influence of environmental medias on crack propagation of a structural steel at high and very high-cycle fatigue (VHCF) regimes is investigated based on the fatigue tests performed in air, water and 3.5% NaCl aqueous solution. Crack…
The development of additive technologies for manufacturing safety‑critical components operating under vibration must be accompanied by a careful analysis of the material’s resistance to high‑cycle fatigue (HCF). This paper presents a…
In a series of applications, steel reinforced concrete structures are subjected to fatigue loads during their service life, what in most cases happens in corrosive environments. Surface treatments have been proved to represent proper…
Paper presents the “in situ” method for determining of irreversible fatigue damage accumulation, based on the analysis of nonlinear manifestations of the feedback signal in a closed system of an ultrasonic fatigue system. During very high…
This work presents an in-depth study of the low-cycle fatigue behaviour of ferritic-pearlitic HSLA-420 high-strength steel sheets, with emphasis on the influence of loading direction on fatigue life and damage mechanisms. Plastic…
This work deals with the notch sensitivity of sharp notches under multi-axial fatigue loading. The main discussion concerns the differences in notch sensitivity at high cycle fatigue regime, between tensile, torsional and combined loading.…
Fatigue life depends strongly on irreversible contributions that accumulate during cyclic loading and unloading of structures. However, the correct identification of the loading path in terms of uniaxial or multi-axial stress states…
Mounting stiffness has an important impact on a system’s structural dynamics and also on the durability of many structures. Mounts with tunable stiffness allow adapting a system’s structural dynamic behavior. Furthermore, they can be used…
Brazing is a widely employed joining technique for aluminium components due to its cost-effectiveness and compatibility with complex geometries. However, the structural integrity of brazed joints under cyclic loading remains a scarcely…
In this paper, high cycle fatigue failure behavior of Load-carrying Cruciform Welded Joints (LCWJ) is assessed using Strain Energy Density (SED) approach. Different analytical solutions are proposed and applied to illustrate the effects of…
Nowadays lifetime calculation in the high cycle fatigue region is commonly based on S/N curves which are modified by different influences to ensure accurate results. Especially the application of these models is important when small…
Two implicit progressive fatigue damage models that rely on new equivalent-damage and equivalent-stress criteria are presented for the prediction of various failure modes of the composites. The criteria are coupled with lamina-based and…
SS 316Ti is widely used in bellows industry and is a good candidate material for high temperature bellows in sodium cooled fast reactor (SFR) systems. Typical operating temperature experienced by SFR systems is around 823K. Design of…
High cycle fatigue tests were conducted for stainless steel AISI 304L. The geometry was a thin walled tube with a passing through hole. The tests were axial, torsional and in-phase axial-torsional, all of them under load control with R =…
We propose the interpretation of the Finite Fracture Mechanics based on the criticality of damage-failure transition due to specific metastability of free energy release. Multiscale mechanisms of fatigue damage-failure transitions in…
A series of strain-controlled multiaxial low cycle fatigue (LCF) tests under proportional and non-proportional loading conditions have been conducted on notched specimens. Cylindrical bars of Al 6061 aluminum alloy and AISI 316L stainless…
Metallic structural components, placed in contact with other bodies while experiencing vibrations in operating conditions, are susceptible to fretting, which can have a significant impact on their fatigue performance. Although extensive…
In this work, the effect of superimposing of isothermal low cycle fatigue loading to the thermomechanical fatigue loading on the crack propagation behavior of the naturally initiated short crack in Low-carbon nitrogen-controlled 316…
This paper examines the influence of controlled heat treatments on the mechanical behaviour of Ti-6Al-4V (Grade 5 Titanium alloy) to improve its performance in structural and high performance applications. Ti-6Al-4V is widely used in…
This study reports an experimental investigation of the fatigue and fracture resistance of R350HT, a heat-treated pearlitic rail steel with refined microstructure used in rails. Monotonic tensile, rotating bending, linear elastic plane…
This work is devoted to an experimental investigation of fatigue behavior of pultruded fiberglass tubes under uniaxial tension, compression and torsion. Static tests were carried out; a presence of postcritical deformation stage during…
Onyx ® is a new material composed of Polyamide 6 reinforced with short carbon fiber, used in the novel additive manufacturing composites technique. This paper aims to present the axial fatigue performance of this material with and without…
A series of fatigue experiments on thin-walled tubes under tension and torsion, the experimental results – crack path and crack growth life – are measured and compared. It is observed that the cracks follow a curvature from a tensile to a…
An experimental campaign was carried out on thin-walled tubes under tension and torsion. The results from experiments are measured and compared. It is observed that cracks follow a shear-dominated growth pattern with increasing crack…
Cracks at notches deserve special consideration in the design of steam turbine components. This work is addressed to investigate the crack initiation behavior a 10%Cr rotor steel with the help of notched specimens under service-type…
Prediction of cyclic life under low cycle fatigue - high cycle fatigue (LCF-HCF) interaction is of paramount importance in the context of structural integrity of components in the primary side of fast reactors where such damage under…
In the last years, a large amount of fatigue test results from plain and bluntly notched specimens made of AISI 304L stainless steel were synthetized in a single scatter band by adopting the specific heat loss per cycle (Q) as a damage…
Automotive industry and mechanical engineering strive to drastically reduce the carbon footprint of their products. This becomes increasingly important as aluminum usage grows for lightweight, efficient components. Nevertheless, cast…
With the introduction of new materials and advances in medical science, the endodontic files have changed since the early days of root canal treatments. In the late days, we have seen an increasing use of Nickel-Titanium (NiTi) alloys, to…
In this work the design and the technical characteristic of a Moore rotating bending machine are presented. The machine has been realized at the University of Cassino in order to run tests on multiple specimens at different temperature.…