The ambient and high-temperature fatigue crack growth behaviors in C(T) and SENT specimens of Ni-based superalloy for turbine disk application were studied in a wide interval of temperatures 25–750°C using a combination a electro- and…
We propose the interpretation of the Finite Fracture Mechanics based on the criticality of damage-failure transition due to specific metastability of free energy release. Multiscale mechanisms of fatigue damage-failure transitions in…
A durability method in view of cathodic protection is proposed to improve the corrosion fatigue resistance of AH 32 steel in seawater. By aid of corrosion fatigue tests, the effects of thermal spraying Zn (zinc) and Cr (chromium) coating…
High cycle fatigue tests were conducted for stainless steel AISI 304L. The geometry was a thin walled tube with a passing through hole. The tests were axial, torsional and in-phase axial-torsional, all of them under load control with R =…
Ultrasonic fatigue tests were carried out on stainless steel AISI 316 and 304, under two modalities: at room temperature and in immersion (water for 316 and antifreeze for 304 steels); all tests were carried out with a loading ratio R=-1.…
A series of strain-controlled multiaxial low cycle fatigue (LCF) tests under proportional and non-proportional loading conditions have been conducted on notched specimens. Cylindrical bars of Al 6061 aluminum alloy and AISI 316L stainless…
The exhaustion of constructive ways for increasing the service life of parts has led to the development of new methods which can improve their material properties during operation under various loading conditions. Laser shock peening (LSP)…
Blades of combustion turbines are extremely loaded turbojet elements, which transmit operative energy onto a rotor. Experiences of many years indicate, that cracks initiation and propagation in the blades during the operation time can…
During a ferry flight, in a standard operation condition and at cruising level, a military cargo experienced a double hydraulic system failure due to a structural damage of the dual booster actuator. The booster actuator is the main…
This investigation revisits biaxial fatigue experiments carried out with the nickel-based superalloy termed Waspaloy. Recently, yield criteria extended to multiaxial fatigue and stress based approaches were analysed and their performance…
Europe has a number of ancient riveted metallic bridges, constructed during the second half of the 19th century up to the middle of the 20th century, which are still in operation. In this paper, a unified approach is presented to generate…
The microstructural origins of premature fatigue failures were investigated on a variety of forged components manufactured from AZ80 and ZK60 magnesium, both at the test specimen level and the full-scale component level. Both stress and…
This study has used the strain energy density (SED) approach to evaluate the stress intensity factor (SIF) of cracked cruciform welded joints in Hardox 450 steel. A microstructural analysis was made of Hardox 450 steel which is composed of…
Power plant piping system subjected to many cyclic loading conditions leads to fatigue loading and thereby crack initiation in the piping system. Demonstrating Leak-Before-Break (LBB) in the design stage itself plays an important role in…
Cyclic stress-strain response and fatigue damage character has been investigated in austenitic stainless steel 316L. Hollow cylindrical specimens have been cyclically deformed in combined tension-compression and torsion under constant…
This paper initially investigates the accuracy of two methods, i.e., the Maximum Variance Method (MVM) and the Maximum Damage Method (MDM), in predicting the orientation of the crack initiation plane in three different metallic materials…
The Equal Channel Angular Pressing is a hardening treatment with which ductile metals can beprocessed to refine their grain and sub-grain structure. This process enhances the mechanical strength of metalsin terms of tensile strength…