Crack closure concept has been widely used to explain different issues of fatigue crack propagation. However, different authors have questioned the relevance of crack closure and have proposed alternative concepts. The main objective here…
It is generally accepted that fatigue crack growth is retarded after an overload, which has been explained either by plasticity-induced crack closure or near-tip residual stress. However, any interpretation of overload effect is…
Fatigue surface crack growth and the in-plane and out-of-plane constraint effects are studied through experiments and computations for aluminium alloy D16T. Subjects for studies are cruciform specimens under different biaxial loading and…
In the current work an experimental study of the crack tip opening displacement (CTOD) is performed to evaluate the ability of this parameter to characterise fatigue crack growth. A methodology is developed to measure and to analyse the…
Fatigue crack growth (FCG) is associated with irreversible and non-linear processes happening at the crack tip. This explains different problems observed in the use of da/dN-?K curves, namely the inability to explain stress ratio and load…
In the last two decades, visual image techniques such as Digital Image Correlation (DIC) enabled to experimentally determine the crack tip displacement and strain fields at small scales. The displacements are tracked during loading, and…
The direct identification of the cohesive law in pure mode I of Pinus pinaster is addressed. The approach couples the double cantilever beam (DCB) test with digital image correlation (DIC). Wooden beam specimens loaded in the…
Fatigue crack growth (FCG) is linked to irreversible and non-linear processes happening at the crack tip, which explains different problems observed in the use of da/dN-DK curves. The replacement of DK by non-linear crack tip parameters…
This paper focusses on discussing equivalent stress intensity factors and kink angles after a change of mode-mixity from one cycle to the next and when the mode-mixity changes continuously during the fatigue cycles. Thin-walled tubes with…
The current work presents an experimental study on the use of the crack tip opening displacement (CTOD) to evaluate its ability to characterise fatigue crack growth. A methodology is developed to measure and to analyse the CTOD from…
In the past two decades, crack-tip mechanics has been increasingly studied with full-field techniques. Within these techniques, Digital Image Correlation (DIC) has been most widely used due to its many advantages, to extract important…
Localized displacement measurements based on electronic speckle-pattern interferometry are used to obtain crack mouth opening displacement (CMOD), stress intensity factor (SIF) and T-stress values during crack growth around cold-expanded…
When the width of cracked nanocomponents made of brittle or quasi-brittle materials is less than approximately , the size of the - dominance zone becomes smaller than and comparable to the fracture process zone ( ). The fracture process…
The three dimensional growth of fatigue cracks in samples of nodular graphite cast iron is characterized using laboratory X-ray computed tomography. The cracks grow from laser machined artificial defects, their development is monitored in…