Multiaxial fatigue behavior is an important topic in critical structural components. In the present study the biaxial-planar fatigue behavior of a powder metallurgical TRIP steel (Transformation Induced Plasticity) was studied by taking…
Stress controlled multiaxial fatigue test was carried out using a hollow cylinder specimen of type 316 stainless steel. A newly developed fatigue testing machine which can apply push-pull loading and reversed torsion loading and inner…
This study discusses fatigue properties of low carbon steel, type SS400 steel, under non-proportional loading. Multiaxial fatigue tests under proportional and non-proportional loading conditions with various stress amplitudes were carried…
T Multiaxial creep-fatigue tests under non-proportional loading conditions with various strain rates were carried out using a hollow cylinder specimen of a high chromium ferritic steel at 823K in air to discuss the influence of…
Multiaxial high cycle fatigue is a topic that concerns nearly all industrial domains. In recent years, a great deal of recommendations how to address problems with multiaxial fatigue life time estimation have been made and a huge progress…
The subject for studies is an aluminium cylindrical hollow specimen with external axial and part circumferential semi-elliptical surface crack undergoing fatigue loads. Both the optical microscope measurements and the crack opening…
This paper discusses features of fatigue crack initiation and growth in aeronautical VT3-1 titanium alloy under pure torsion loading in gigacycle regime. Two materials: extruded and forged VT3-1 titanium alloys were studied. Torsion…
A series of cyclic tension-torsion tests under symmetric shear strain and asymmetric axial stress control in various loading paths are conducted on 100 ?m-diameter 316L steel wires applying a micro tensiontorsion fatigue testing apparatus.…
The experimental study presented in this research was conducted to understand the performance of rubberized concrete columns under axial loads and numerically analyze the conduct of rubberized reinforced concrete (RRC) columns under cyclic…
Components and structures are designed based in their material’s mechanical properties such as Young's modulus or yield stress among others. Often those properties are obtained under monotonic mechanical tests but rarely under cyclic ones.…
Fatigue life tests under constant and variable amplitude loadings were performed on the tube-tube thin-walled welded specimens made of magnesium (AZ31 and AZ61) alloys. The tests included pure axial, pure torsional and combined in-phase…
An edge crack propagation in a steel bar of circular cross-section undergoing multiaxial fatigue loads is simulated by Finite Element Method (FEM). The variation of crack growth behaviour is studied under axial and combined in phase…
The fatigue behavior of carburized components such as automotive transmission gears is very complex due to hardness and microstructure difference, residual stresses and multi-axial stress states developed between the case and the core. In…
The aim of the present paper is the investigation of temporal instabilities and spatial localization due to the Lüders behavior, the Portevin–Le Chatelier effect and the shoulder or necking effect during uniaxial tension tests of…
Multiaxial fatigue is a challenging problem and, consequently, a number of methods has been developed to aid in design of components and assemblies. Following the complexity of the problem, these approaches are often elaborate and it is…
Cracks at notches deserve special consideration in the design of steam turbine components. This work is addressed to investigate the crack initiation behavior a 10%Cr rotor steel with the help of notched specimens under service-type…
This study compares both uniaxial and multiaxial variable amplitude experimental crack growth data for naturally initiated fatigue cracks in tubular specimens of 2024-T3 aluminum alloy to predictions based on two state-of-the-art analysis…
This paper deals with the influence of the cold drawing process on the fracture behaviour of pearlitic steels. To this end, fracture tests under axial loading were performed on steel wires with different drawing degree (from a hot rolled…
Reinforced concrete (RC) columns cannot get supreme confinement by using the customary steel stirrups reinforcement because of the requirements for the spacing distances between the stirrups in addition to concrete continuance trouble. For…
Concrete Filled Double Skinned Steel Tubular (CFDST) composite column is preferred over Concrete Filled Steel Tube composite column (CFST) owing to enhanced strength. However, they may possess concrete imperfection due to shrinkage and…
The work reports the observed fatigue damage of C45 steel specimens tested in a previous work under multiaxial loading conditions and its relationship with the thermal energy dissipation which has been used in the last decades to estimate…
In this paper, the stress intensity factor (SIF) is computed in a circumferentially-cracked round bar (CCRB) subjected to tensile loading, considering that the resistant ligament is circular and exhibits certain eccentricity in relation to…
Fatigue crack initiation and propagation involve plastic strains that require some work to be done on the material. Most of this irreversible energy is dissipated as heat and consequently the material temperature increases. The heat being…
This paper deals with the fatigue assessment of cast steel defects in terms of macroscopic shrinkage porosity. Within preliminary studies, a generalized Kitagawa diagram GKD was established by numerical analyses of V-notched specimens with…
This paper presents numerical models of a 3D printed plastic joint applicable to the connection of wooden structures. The research presented provides a comparison of two alternative solutions for the geometry of the joint and results from…
Onyx ® is a new material composed of Polyamide 6 reinforced with short carbon fiber, used in the novel additive manufacturing composites technique. This paper aims to present the axial fatigue performance of this material with and without…
Axial alternating fatigue tests with superimposed static torsional mean stress and shear alternating fatigue tests with superimposed static tensile mean stress are represented. A decrease in the fatigue life of the material was observed…
In this article, the characteristic curves of microindentation measured on Cu99 were analyzed on the basis of the analytical expression proposed by Habibi et al. (J. Mater. Res, 2021, 36 (15): 3074-3085). It was found that the ratio of the…
This paper deals with the influence of interference fit coupling on the fatigue strength of holed plates. The effect was investigated both experimentally and numerically. Axial fatigue tests have been carried out on holed specimens made of…
Safety Impact resistance is defined as the ability of a material to absorb impact energy through controlled failure mechanism. The greater the energy absorption by the crash safety structure, the greater the safety in preventing…
Paper presents the analytical solution of the stress-strain state for a dented pipeline, based on the method of equivalent loads. First off all solution for a harmonic imperfection is found, then using Fourier series expansion a…