SI: IGF26 - 26th International Conference on Fracture and Structural Integrity Views: 755 Downloads: 661 Vol. 16, No. 59 (2022) December 22, 2021 pp. 359-373

A probabilistic fatigue crack growth life approach to the definition of inspection intervals for railway axles

C. Mallor, S. Calvo, J.L. Nuñez, R. Rodriguez-Barrachina, A. Landaberea

Different options that rely on fracture mechanics are currently used in engineering during the design and assessment of components. One of the most important aspects is the time taken for a crack to extend to its critical size. If this…

10.3221/IGF-ESIS.59.24

Details: A probabilistic fatigue crack growth life approach to the definition of inspection intervals for railway axles PDF Visual Abstract

PDF Visual Abstract

Miscellanea Views: 955 Downloads: 423 Vol. 13, No. 47 (2019) December 1, 2018 pp. 65-73

The thermal damaging process of diorite under microwave irradiation

Xirui Lu, Chen Yuan, Zeng Junsen, Hu Qijun, Shao Dadong, Zhang Haibin, Lu Xirui

Laboratory tests have been conducted to investigate the effects of thermal damage on diorite under microwave irradiation. The sample rocks were heated to high temperature range of 300 to 800 ℃ in a single-mode microwave furnace. The…

10.3221/IGF-ESIS.47.06

Details: The thermal damaging process of diorite under microwave irradiation PDF Visual Abstract

PDF Visual Abstract

SI: Damage Mechanics of materials and structures Views: 591 Downloads: 462 Vol. 19, No. 72 (2025) March 24, 2025 pp. 247-262

Predicting the strength of 3D-printed conductive composite under tensile load: A probabilistic modeling and experimental study

Nassima Naboulsi, Fatima Majid, Taoufik Hachimi, Najoua Barhoumi, Kaouthar Khlifi, Soufyan Dadoun

Conductive PLA is an innovative composite material that combines the ecological benefits of polylactic acid, a biodegradable thermoplastic, with electrical conductivity properties. Usually used in additive manufacturing for its ease of…

10.3221/IGF-ESIS.72.18

Details: Predicting the strength of 3D-printed conductive composite under tensile load: A probabilistic modeling and experimental study PDF HTML Visual Abstract

PDF HTML Visual Abstract

SI: Fracture Mechanics versus Environment Views: 573 Downloads: 491 Vol. 13, No. 50 (2019) July 17, 2019 pp. 98-111

Environmental effects on the reliability of an AISI 304 structure

Racim Boutelidja, Abdelmoumene Guedri, Mohammed Amine Belyamna, Bachir Merzoug

This work is based on the application of probabilistic fracture mechanics (MRP) models to predict the reliability of pressure pipelines in nuclear power reactors. The simulation of cracking of stainless steel piping under the conditions of…

10.3221/IGF-ESIS.50.10

Details: Environmental effects on the reliability of an AISI 304 structure PDF Visual Abstract

PDF Visual Abstract

Advanced Manufacturing and Processing Views: 915 Downloads: 1,130 Vol. 16, No. 62 (2022) September 22, 2022 pp. 385-407

Synthesis, Microstructural Characterization, Mechanical, Fractographic and Wear Behavior of Micro B4C Particles Reinforced Al2618 Alloy Aerospace Composites

Veeresha G, Manjunatha B, V. Bharath, M Nagaral, VAuradi

In the current studies an investigations were made to know the effect of 63 micron sized B₄C particles addition on the mechanical and wear behavior of aerospace alloy Al2618 metal composites. Al2618 alloy with different weight percentages…

10.3221/IGF-ESIS.62.27

Details: Synthesis, Microstructural Characterization, Mechanical, Fractographic and Wear Behavior of Micro B4C Particles Reinforced Al2618 Alloy Aerospace Composites PDF Visual Abstract

PDF Visual Abstract

Miscellanea Views: 931 Downloads: 529 Vol. 11, No. 42 (2017) September 29, 2017 pp. Pages 272-279

Investigation on some factors affecting crack formation in high resistance aluminum alloys

A. Brotzu, F. Felli, D. Pilone

Aluminum alloys having good mechanical properties are Al-Zn- Mg alloys (7xxx) and Al-Cu-Li alloys (Weldalite®). These alloys may be subjected to stress corrosion cracking. In order to overcome this problem the Al 7050 alloy has been…

10.3221/IGF-ESIS.42.29

Details: Investigation on some factors affecting crack formation in high resistance aluminum alloys PDF

PDF

Miscellanea Views: 1,367 Downloads: 843 Vol. 12, No. 44 (2018) March 21, 2018 pp. 140-150

Modification of the Bonora Damage Model for shear failure

Nicola Bonora, Gabriel Testa, Andrew Ruggiero, Gianluca Iannitti, Domenico Gentile

The Bonora damage model was extended to account for shear-controlled damage. To this purpose, a new definition for the damage dissipation potential in which an explicit dependence on the third invariant of deviatoric stress was proposed.…

10.3221/IGF-ESIS.44.11

Details: Modification of the Bonora Damage Model for shear failure PDF

PDF

Search the articles

Search results

A probabilistic fatigue crack growth life approach to the definition of inspection intervals for railway axles

The thermal damaging process of diorite under microwave irradiation

Predicting the strength of 3D-printed conductive composite under tensile load: A probabilistic modeling and experimental study

Environmental effects on the reliability of an AISI 304 structure

Synthesis, Microstructural Characterization, Mechanical, Fractographic and Wear Behavior of Micro B4C Particles Reinforced Al2618 Alloy Aerospace Composites

Investigation on some factors affecting crack formation in high resistance aluminum alloys

Modification of the Bonora Damage Model for shear failure