In this work it is proposed a methodology for the evaluation of plasticity-induced crack shielding from the analysis of the crack tip displacements fields measured by digital image correlation. This methodology is based on the evaluation…
According to Gradient Mechanics (GM), stress fields have to be determined by directly incorporating into the stress analysis a length scale which that takes into account the material microstructural features. This peculiar modus operandi…
Fields of stress, strain rate and process zone of a mode I creep crack growth are analyzed by employing damage evolution equations. Damage models for fracture of process zone represented by stress based formulation. Two expressions are…
A study on the approximation of the stress field in the vicinity of crack tip in a compact tension specimen made from Al 2024-T351 is presented. Crack tip stress tensor components are expressed using the linear elastic fracture mechanics…
For wedge splitting test specimens, the stress and displacement fields both in the vicinity and also in larger distance from the crack tip are investigated by means of numerical methods. Several variants of boundary conditions were…
The current work presents a novel methodology for the experimental quantification of the crack tip plastic zone during fatigue crack growth. This methodology is based on the application of yield criteria to estimate the area and the shape…
Notches and cracks are usually approximately modeled as two-dimensional problems using solutions from plane elasticity to quantify localized stress/strain concentration effects around their tips. However, they may be associated with high…
A quality of multi-parameter approximation of the stress and displacement fields around a crack tip in a non-brittle material test specimen is studied in the paper. The stress field approximation using Williams power series is intended to…
In the last two decades, visual image techniques such as Digital Image Correlation (DIC) enabled to experimentally determine the crack tip displacement and strain fields at small scales. The displacements are tracked during loading, and…
A class of fatigue crack growth models based on elastic–plastic stress–strain histories at the crack tip region and local strain-life damage models have been proposed in literature. The fatigue crack growth is regarded as a process of…
Crack closure influences fatigue crack growth rate and must be included in the design of components. Plasticity induced crack closure is intimately linked with the crack tip plastic deformation, which becomes residual as the crack…
This paper focusses on discussing equivalent stress intensity factors and kink angles after a change of mode-mixity from one cycle to the next and when the mode-mixity changes continuously during the fatigue cycles. Thin-walled tubes with…
The paper analyses previously reported work, which uses digital image correlation to measure fatigue crack closure. As well as determining crack opening loads, the information on crack shape may be used to estimate the stress intensity…
In this paper Digital Image Correlation (DIC) is used to study the evolution of the plastic zone close to a crack tip. A modified CT-specimen was used in order to fulfill the plane stress condition. The strain field around the crack tip…
This paper is devoted to the analysis of the load path effect on I+II+III mixed mode fatigue crack propagation in a 316L stainless steel. Experiments were conducted in mode I+II and in mode I+II+III. The same maximum, minimum and mean…
This paper deals with the influence of the cold drawing process on the fracture behaviour of pearlitic steels. To this end, fracture tests under axial loading were performed on steel wires with different drawing degree (from a hot rolled…
The current work presents an experimental study on the use of the crack tip opening displacement (CTOD) to evaluate its ability to characterise fatigue crack growth. A methodology is developed to measure and to analyse the CTOD from…
For various configurations examined in a series of fatigue experiments on thin-walled tubes under tension and torsion, the experimental results – crack path, crack growth life, near crack tip deformations, and crack closure – are measured…
The plastic zone is theoretically and numerically analyzed for various combinations of the nonsingular terms xx T to zz T ratios in connection with specimen thickness under mode I loading. The plastic zone size distribution is based on the…
A study on the accuracy of the approximation of the displacement field around of crack tip in a sample made from bridge steel (S355) is main objective of contribution. Linear elastic fracture mechanics (LEFM) theory in framework of…
The present contribution reviews a recently proposed method to rapidly estimate the averaged SED at the tip of short as well as long cracks under in-plane I+II and long cracks under out-of-plane I+III mixed mode loadings. Short cracks are…
When the width of cracked nanocomponents made of brittle or quasi-brittle materials is less than approximately , the size of the - dominance zone becomes smaller than and comparable to the fracture process zone ( ). The fracture process…
In real industrial conditions, it’s common to witness the interaction of multiple cracks such that their stress fields and crack driving forces are disturbed. For coplanar cracks, a greater hazard is expected because of the amplification…