Fatigue tests run-out specimens up to 106 – 5x107 load cycles are used to determine the stress level named “fatigue limit”. Nevertheless, it is not clear what kind of fatigue cracking takes or will take place in these specimens. To discuss…
The stress, strain rate and process zone with respect to the creep-crack growth are analyzed by employing damage-evolution equations. The damage models for the fracture of the process zone are represented using a stress and ductility based…
An edge crack propagation in a steel bar of circular cross-section undergoing multiaxial fatigue loads is simulated by Finite Element Method (FEM). The variation of crack growth behaviour is studied under axial and combined in phase…
In recent years, mechanical property of many SMA has improved in order to introduce these alloys in specific field of industry. Main examples of these alloys are the NiTi, Cu-Zn-Al and Cu-Al-Ni which are used in many fields of engineering…
In this paper, the macro and micro-mechanical fracture behavior was studied for aluminum (Al6061) alloy matrix, reinforced with various proportions of TiC particles such as 3wt%, 5wt% and 7wt%. The Al6061-TiC metal matrix composites were…
Fatigue (high- and gigacycle) crack initiation and its propagation in titanium alloys with coarse and fine grain structure are studied by fractography analysis of fracture surface. Fractured specimens were analyzed by interferometer…
In this study, a numerical strategy for predictive modelling of creep in tension tests for the rectangular plate with a single crack and CT-specimen based on the extended finite element method (XFEM) will be described in detail. A model of…
There is a tremendous increase in the use of high strength and high performance self-consolidating cementitious composites due to their superior workability and mechanical strengths. Cement composites are quasi-brittle in nature and…
Elber assumed that the actual driving force for fatigue crack growth (FCG) is the effective stress intensity factor ΔKeff. To verify this hypothesis, both DC(T) and C(T) specimens are cut from a 6351-T6 Al alloy circular bar with two…
A double cantilever beam geometry has been chosen in order to investigate the importance of the higher-order terms of the Williams’ power expansion for the crack path estimation. The crack propagation has been tested experimentally on a…
Variational principle of brittle fracture mechanics is employed to predict the crack path in an infinite wedge under a concentrated tensile force. The weight function in basic equation of variational problem is assumed to be proportional…
The present work aims at developing a new approach towards the analysis of the crack path through the access to the information from the infrared (IR) video imaging of the steady fatigue crack growth. We first test some commonly available…
This paper focusses on discussing equivalent stress intensity factors and kink angles after a change of mode-mixity from one cycle to the next and when the mode-mixity changes continuously during the fatigue cycles. Thin-walled tubes with…
The present work aims to model the fracture mechanical behavior of a high-strength low carbon steel, AISI 4130 operating in hydrogen contaminated environment. The study deals with the development of 2D finite element cohesive zone model…
This paper provides the background for practical applications of nonlinear fracture resistance parameters for structural integrity assessment of aviation structures with initial cracks. The subject of this numerical study is a fragment of…
Mixed mode crack propagation analysis has been more accessible with the development of new numerical tools, allowing to evaluate the influence of non-mode I loadings in the crack path and in the growth rate. The aim of this work is to…
Nowadays the demand for high strength steels is increasing. In order to design and develop high performance products, it is essential to understand the fatigue behavior of these materials. When considering welded components, the fatigue…
The profile samples prepared by focused ion beam (FIB) in crack initiation region (CIR) and fish-eye (FiE) region of failed specimens subjected to rotary bending (RB) and ultrasonic axial (UL) fatigue testing with various stress ratios (R)…
A geometrically simplified plane elasticity problem of a finite small crack emanating from a thin interfacial zone surrounding the circular inclusion situated in the finite bounded domain is investigated. The crack is arbitrarily oriented…
The most important performance for repair materials is adhesion to the substrate. The authors experimentally find out that high modulus fine aggregates in repair material enhance strength of it as well as the strength of the interface…
This paper deals with the influence of the cold drawing process on the fracture behaviour of pearlitic steels. To this end, fracture tests under axial loading were performed on steel wires with different drawing degree (from a hot rolled…
Blades of combustion turbines are extremely loaded turbojet elements, which transmit operative energy onto a rotor. Experiences of many years indicate, that cracks initiation and propagation in the blades during the operation time can…
This paper presents an application of the boundary element method to the analysis of crack growth problems in linear elastic fracture mechanics and the correlation of results with experimental data. The methodology consists of computing…
Two cracks, initiated from the opposite tips of a central notch inclined by 45°, were considered in cruciform specimens made of Ti6246. A static load was applied to a cruciform arm while a cyclic load was applied along the other arm.…
Rebar corrosion significantly affects the overall performance and the service life of reinforced concrete (RC) structures due to the reduction in the bond strength between concrete and rebar, leading to the delamination of the concrete…
A 2D bond-breaking model is presented that allows the extraction of the intrinsic line or edge energy, fracture toughness, and strain energy release rate of graphene from measured and calculated 2D Young’s moduli and 2D pristine strengths.…
This paper deals with the fatigue assessment of cast steel defects in terms of macroscopic shrinkage porosity. Within preliminary studies, a generalized Kitagawa diagram GKD was established by numerical analyses of V-notched specimens with…
In this work, the effects of natural particles on the micro failure mechanisms and static strength of an epoxy are studied using scanning electron microscope (SEM) technique. To this end, bulk specimens and adhesively bonded single lap…
The fracture behavior of quasi-brittle materials such as concrete is characterized by the presence of a fracture process zone (FPZ) that precedes the main crack. Within this zone, various mechanisms, including the formation of microcracks…
The use of temporary hip prosthesis made of orthopedic cement (spacer) in conjunction with antibiotics became a prevalent method used for prosthetic infections remedy; consequently, this method makes bone cement (PMMA) more fragile. Hence…
Elastic fracture mechanics commonly defines the fracture resistance of brittle materials within an idealised picture of planar and traction free cracks. An efficient approach to describe the interface conditions in real cracks, such as…
In this study, an efficient computational method for modeling the transition from transgranular to intergranular fracture mechanisms based on phase field fracture theory is discussed. Structural heterogeneity of the material is modeled on…
The present paper is devoted to an experimental study on the fracture behaviour of natural stones, commonly used as elements for building cladding, under both monotonic and cyclic loading, with particular emphasis to white Carrara marble.…